DOW™ LDPE 535I
| Category: | LDPE , Low Density Polyethylene Resin |
| Manufacturer: | The Dow Chemical Company |
| Trademark: | DOW™ LDPE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | bK3zlp_DOW-LDPE-535I.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
| General Information | |
|---|---|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.925 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 1.9 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 51 | µm | |
| Film Puncture Resistance (51 µm) | 2.90 | J/cm³ | Internal method |
| Film strength | ASTM D882 | ||
| MD : 51 µm | 196 | J/cm³ | ASTM D882 |
| TD : 51 µm | 207 | J/cm³ | ASTM D882 |
| Tensile Strength | ASTM D882 | ||
| MD : Yield, 51 µm | 13.6 | MPa | ASTM D882 |
| TD : Yield, 51 µm | 13.7 | MPa | ASTM D882 |
| MD : Fracture, 51 µm | 25.0 | MPa | ASTM D882 |
| TD : Fracture, 51 µm | 21.1 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Fracture, 51 µm | 550 | % | ASTM D882 |
| TD : Fracture, 51 µm | 770 | % | ASTM D882 |
| Dart Drop Impact (51 µm) | 86 | g | ASTM D1709A |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 51 µm | 360 | g | ASTM D1922 |
| TD : 51 µm | 470 | g | ASTM D1922 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 97.8 | °C | ASTM D1525 |
| Melting Temperature (DSC) | 114 | °C | Internal method |
| Optical | Nominal Value | Test Method | |
|---|---|---|---|
| Gloss (45°, 50.8 µm) | 72 | ASTM D2457 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 216 | °C |
| Extrusion instructions |
|---|
| 吹塑薄膜的制造条件： 螺杆尺寸：2.5 英寸 (63.5 mm)；24:1 L/D 螺杆类型：带 Maddock Mixer 的单跨型 模具间隙：40 密尔 (1.0 mm) 熔体温度：420 °F (216 °C) 输出：模具周长的 10 磅/小时/英寸 模具直径：6 英寸 放大比：2.5:1 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Romiloy® 1055 F PG | ROMIRA GmbH | PC+ABS | Romiloy® |
| Taitarex® 818K | Taita Chemical Company, Ltd. | PS (GPPS) | Taitarex® |
| Vistalon™ 3702 | ExxonMobil Chemical | EPDM | Vistalon™ |
| ColorRx® PP2-0190RX | LTL Color Compounders, Inc. | PP Random Copolymer | ColorRx® |
| LNP™ THERMOCOMP™ UF006AS compound | SABIC Innovative Plastics | PPA | LNP™ THERMOCOMP™ |