LNP™ FARADEX™ NX07344 compound
| Category: | PC+ABS , Polycarbonate + ABS |
| Manufacturer: | SABIC Innovative Plastics Asia Pacific |
| Trademark: | LNP™ FARADEX™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | bHxaPo_LNP-FARADEX-NX07344-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Faradex NX07344 is a compound based on PC+ABS blend resin containing non-brominated and non-chlorinated flame retardant system, Stainless Steel and glass fiber. Added features of this material include: EMI/RFI Shielding and ESD. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.46 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | Internal Method | ||
| Flow | 0.38 | % | |
| Across Flow | 0.46 | % | |
| Water Absorption | |||
| 24 hr, 50% RH | 0.080 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.040 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 6000 | MPa | ASTM D638 |
| -- | 5800 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Break 2 | 60.0 | MPa | ASTM D638 |
| Break | 62.0 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Break 3 | 1.8 | % | ASTM D638 |
| Break | 1.8 | % | ISO 527-2/5 |
| Flexural Modulus 4(50.0 mm Span) | 5300 | MPa | ASTM D790 |
| Flexural Stress | |||
| -- | 105 | MPa | ISO 178 |
| Yield, 50.0 mm Span 5 | 90.0 | MPa | ASTM D790 |
| Break, 50.0 mm Span 6 | 90.0 | MPa | ASTM D790 |
| Flexural Strain at Break 7 | 2.8 | % | ISO 178 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shielding Effectiveness | Internal Method | ||
| 1.50 mm | 47 to 53 | dB | |
| 3.00 mm | 60 to 70 | dB | |
| Static Decay 8 | 10 | msec | FTMS 101B |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 9(23°C) | 7.6 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact | |||
| -30°C | 44 | J/m | ASTM D256 |
| 23°C | 60 | J/m | ASTM D256 |
| -30°C 10 | 5.3 | kJ/m² | ISO 180/1A |
| 23°C 11 | 6.0 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| -30°C | 330 | J/m | ASTM D4812 |
| 23°C | 350 | J/m | ASTM D4812 |
| -30°C 12 | 21 | kJ/m² | ISO 180/1U |
| 23°C 13 | 21 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Total Energy | 11.5 | J | ASTM D3763 |
| -- | 4.30 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, Unannealed, 3.20 mm | 94.0 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 6.40 mm | 96.0 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 14 | 96.0 | °C | ISO 75-2/Af |
| Vicat Softening Temperature | |||
| -- | 101 | °C | ASTM D1525 15 |
| -- | 105 | °C | ASTM D1525, ISO 306/B120 13 16 |
| -- | 102 | °C | ISO 306/A50 |
| CLTE | |||
| Flow : -40 to 40°C | 3.1E-5 | cm/cm/°C | ASTM E831 |
| Flow : 23 to 60°C | 2.9E-5 | cm/cm/°C | ISO 11359-2 |
| Transverse : -40 to 40°C | 5.8E-5 | cm/cm/°C | ASTM E831 |
| Transverse : 23 to 60°C | 7.4E-5 | cm/cm/°C | ISO 11359-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+3 to 1.0E+6 | ohms | ASTM D257 |
| Volume Resistivity | 1.0E+4 to 1.0E+6 | ohms·cm | ASTM D257 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.50 mm) | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 85.0 to 90.0 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Suggested Max Moisture | 0.040 | % | |
| Rear Temperature | 260 to 300 | °C | |
| Middle Temperature | 260 to 300 | °C | |
| Front Temperature | 265 to 300 | °C | |
| Nozzle Temperature | 265 to 300 | °C | |
| Processing (Melt) Temp | 270 to 300 | °C | |
| Mold Temperature | 60.0 to 100 | °C | |
| Back Pressure | 4.00 | MPa | |
| Screw Speed | 30 to 100 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | 1.3 mm/min |
| 5 . | 1.3 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 2 mm/min |
| 8 . | 5000V to <50V |
| 9 . | 80*10*4 sp=62mm |
| 10 . | 80*10*4 |
| 11 . | 80*10*4 |
| 12 . | 80*10*4 |
| 13 . | 80*10*4 |
| 14 . | 80*10*4 mm |
| 15 . | Rate A (50°C/h), Loading 2 (50 N) |
| 16 . | Rate B (120°C/h), Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TEREZ PA 6 7500 GF 20 GK 10 | TER HELL PLASTIC GMBH | Nylon 6 | TEREZ PA 6 |
| NYLOY® KF-0010N 2140B | Nytex Composites Co., Ltd. | Nylon, Unspecified | NYLOY® |
| Daelim Po1y® LL-05SU | DAELIM INDUSTRIAL CO., LTD. | LLDPE | Daelim Po1y® |
| Sylvin 8240-95FU White 1512 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Sylvin 7833-70C Red 6199 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |