Niretan B F50
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Soredi S.p.a. |
| Trademark: | Niretan B |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | bHCcCT_Niretan-B-F50.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Polyamide 6 reinforced with 50% glass fibre, for injection moulding |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Forms |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Specific Gravity | 1.56 | -- | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 0.40 to 1.0 | -- | % | ASTM D955 |
| Water Absorption | ASTM D570 | |||
| 23°C, 24 hr | 6.0 | -- | % | |
| Equilibrium, 23°C, 50% RH | 2.0 | -- | % |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Rockwell Hardness (R-Scale) | 110 | 90 | ASTM D785 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Strength 1(Break) | 210 | 130 | MPa | ASTM D638 |
| Tensile Elongation 2(Break) | 2.0 | 4.0 | % | ASTM D638 |
| Flexural Modulus 3 | 13500 | 9500 | MPa | ASTM D790 |
| Flexural Strength 4(Break) | 200 | 130 | MPa | ASTM D790 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Notched Izod Impact | ASTM D256 | |||
| -20°C, 3.20 mm | 90 | 150 | J/m | |
| 23°C, 3.20 mm | 180 | 240 | J/m |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 190 | -- | °C | ASTM D648 |
| Peak Crystallization Temperature (DSC) | 220 | -- | °C | ASTM D3418 |
| CLTE - Flow (23 to 55°C) | 5.0E-5 | -- | cm/cm/°C | ISO 11359-2 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | 1.0E+14 | 1.0E+13 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+15 | 1.0E+12 | ohms·cm | IEC 60093 |
| Electric Strength (1.00 mm) | 34 | 24 | kV/mm | IEC 60243-1 |
| Relative Permittivity (1 MHz) | 3.80 | 4.20 | IEC 60250 | |
| Dissipation Factor (1 MHz) | 0.020 | 0.12 | IEC 60250 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating | UL 94 | |||
| 1.60 mm | HB | -- | ||
| 3.20 mm | HB | -- | ||
| Glow Wire Ignition Temperature (2.00 mm) | 650 | -- | °C | IEC 60695-2-13 |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | 5.0 mm/min |
| 3 . | 1.3 mm/min |
| 4 . | 1.3 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 685 HB | RTP Company | ABS | RTP |
| SOLPLAST TH 9000B | UTEKSOL d.o.o. | SBS | SOLPLAST TH |
| Niuk 60RNG30 | Shanghai Niuk New Plastic Technology Co., Ltd. | PBT | Niuk |
| ESTAPROP 1020 | Cossa Polimeri S.r.l. | PP Homopolymer | ESTAPROP |
| LNP™ COLORCOMP™ W10009I compound | SABIC Innovative Plastics Europe | PBT | LNP™ COLORCOMP™ |