LNP™ THERMOCOMP™ AF004AH compound
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ THERMOCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | bGsVGP_LNP-THERMOCOMP-AF004AH-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP THERMOCOMP* AF004AH is a compound based on ABS resin containing 20% Glass Fiber. Added feature of this material is: Healthcare. Also known as: LNP* THERMOCOMP* Compound AF-1004 Product reorder name: AF004AH |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.19 | g/cm³ | ISO 1183, ASTM D792 |
| Molding Shrinkage | |||
| Flow : 24 hr | 0.20 | % | ASTM D955 |
| Across Flow : 24 hr | 0.40 | % | ASTM D955, ISO 294-4 |
| Flow : 24 hr | 0.24 | % | ISO 294-4 |
| Water Absorption | |||
| 24 hr, 50% RH | 0.24 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.39 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 6170 | MPa | ASTM D638 |
| -- | 6000 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Break 2 | 70.0 | MPa | ASTM D638 |
| Break | 81.0 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Break 3 | 2.2 | % | ASTM D638 |
| Break | 2.0 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0 mm Span 4 | 6150 | MPa | ASTM D790 |
| -- 5 | 5860 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 123 | MPa | ISO 178 |
| Break, 50.0 mm Span 6 | 130 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 80 | J/m | ASTM D256 |
| 23°C 7 | 8.0 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 400 | J/m | ASTM D4812 |
| 23°C 8 | 23 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Total Energy | 11.0 | J | ASTM D3763 |
| -- | 3.00 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, Unannealed, 3.20 mm | 103 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 9 | 93.0 | °C | ISO 75-2/Af |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.50 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.050 to 0.10 | % | |
| Rear Temperature | 204 to 216 | °C | |
| Middle Temperature | 232 to 243 | °C | |
| Front Temperature | 266 to 277 | °C | |
| Processing (Melt) Temp | 260 | °C | |
| Mold Temperature | 71.1 to 82.2 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | 1.3 mm/min |
| 5 . | 2.0 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 80*10*4 |
| 8 . | 80*10*4 |
| 9 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TECHNYL® C 218 MZ20 V10 BLACK Z | Solvay Engineering Plastics | Nylon 6 | TECHNYL® C |
| Monprene® OM-12252 | Teknor Apex Company | TPE | Monprene® |
| VITAMIDE® AI12 | A. Schulman Europe | Nylon 66 | VITAMIDE® |
| Bluestar Epoxy EX-27D | Bluestar New Chemical Materials Co. Ltd | Epoxy | Bluestar Epoxy |
| DURAFIDE® 6165A4 | Polyplastics Co., Ltd. | PPS | DURAFIDE® |