Order Products : sales@su-jiao.com
PLUSTEK PA320G6
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Polyram Ram-On Industries |
| Trademark: | PLUSTEK |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | bGX9tp_PLUSTEK-PA320G6.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 30% GLASS-FIBER REINFORCED, FLAME RETARDANT POLYAMIDE 6.6 FOR INJECTION MUOLDING APPLICATIONS. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.38 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | |||
| Flow | 0.30 - 0.70 | % | ASTM D955 |
| -- | 0.30 - 0.70 | % | ISO 2577 |
| Water Absorption | |||
| Saturation | 4.5 | % | ASTM D570 |
| Saturated, 23°C | 4.5 | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 1.5 | % | ASTM D570, ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness | |||
| Class r | 122 | ASTM D785 | |
| R scale | 122 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 150 | MPa | ASTM D638, ISO 527-2 |
| Tensile Elongation (Break) | 2.0 | % | ASTM D638, ISO 527-2 |
| Flexural Modulus | 8000 | MPa | ASTM D790, ISO 178 |
| Flexural Strength | 200 | MPa | ASTM D790, ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 110 | J/m | ASTM D256 |
| 23°C | 12 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, not annealed | 238 | °C | ASTM D648, ISO 75-2/B |
| 1.8 MPa, not annealed | 225 | °C | ASTM D648, ISO 75-2/A |
| Melting Temperature | 256 | °C | ISO 11357-3, ASTM D3417 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+13 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+17 | ohms·cm | IEC 60093 |
| Dielectric Strength | 80 | kV/mm | IEC 60243-1 |
| Dielectric Constant (1 MHz) | 3.70 | IEC 60250 | |
| Comparative Tracking Index | 325 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.60 mm | V-0 | UL 94 | |
| 3.00 mm | V-0 | UL 94 | |
| Glow Wire Flammability Index (1.60 mm) | 960 | °C | IEC 60695-2-12 |
| Glow Wire Ignition Temperature (1.60 mm) | 825 | °C | IEC 60695-2-13 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 85.0 | °C | |
| Drying Time | 3.0 | hr | |
| Suggested Max Moisture | 0.15 | % | |
| Rear Temperature | 270 - 280 | °C | |
| Middle Temperature | 280 - 300 | °C | |
| Front Temperature | 285 - 310 | °C | |
| Mold Temperature | 65.0 - 110 | °C | |
| Injection Pressure | 70.0 - 125 | MPa | |
| Injection Rate | Fast | ||
| Holding Pressure | 35.0 - 85.0 | MPa | |
| Back Pressure | 0.350 - 0.700 | MPa | |
| Screw Speed | 60 - 90 | rpm |
| Injection instructions |
|---|
| Fill Speed: 50 to 75 mm/sec |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SUSTARIN® C | Röchling Sustaplast SE & Co. KG | Acetal (POM) Copolymer | SUSTARIN® |
| TOTAL Polyethylene Lotrène® Q2018 H | TOTAL Refining & Chemicals | LLDPE | TOTAL Polyethylene |
| ASI POLYETHYLENE CP 851 | A. Schulman Inc. | LDPE | ASI POLYETHYLENE |
| Sylvin 9917-89 Black | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| LEXAN™ 221R resin | SABIC Innovative Plastics | PC | LEXAN™ |