THERMORUN® 3755B/N
| Category: | TPE , Thermoplastic Elastomer |
| Manufacturer: | Mitsubishi Chemical Performance Polymers, Inc. |
| Trademark: | THERMORUN® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | bGSPYb_THERMORUN-3755B-N.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| THERMORUN®3755B/N is a thermoplastic elastomer (TPE) material,. This product is available in North America, Europe or Asia Pacific. The processing method is extrusion or injection molding. THERMORUN®The main characteristics of 3755B/N are: low hardness. |
| General Information | |
|---|---|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.880 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/5.0 kg) | 4.0 | g/10 min | ISO 1133 |
| Molding Shrinkage | ISO 294-4 | ||
| Vertical flow direction | 1.5 - 2.0 | % | ISO 294-4 |
| Flow direction | 1.5 - 2.0 | % | ISO 294-4 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore A) | 75 | ISO 868 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ISO 37 | ||
| 100% strain | 3.30 | MPa | ISO 37 |
| 300% strain | 4.40 | MPa | ISO 37 |
| Tensile Stress (Break) | 10.0 | MPa | ISO 37 |
| Tensile Elongation (Break) | 730 | % | ISO 37 |
| Tear Strength | 47 | kN/m | ISO 34-1 |
| Compression Set (70°C, 22 hr) | 46 | % | ISO 815 |
| Additional Information |
|---|
| Data obtained using JIS test methods. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 287B | RTP Company | Nylon 610 | RTP |
| Sindustris PBT GP1001D | Sincerity Australia Pty Ltd. | PBT | Sindustris PBT |
| Ultramid® A3L HP | BASF Corporation | Nylon 66 | Ultramid® |
| Di-Pak™ E-4665 | Hapco Inc. | TP, Unspecified | Di-Pak™ |
| LEXAN™ LS2 resin | SABIC Innovative Plastics | PC | LEXAN™ |