Aegis® H8202NLB
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Honeywell |
| Trademark: | Aegis® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | bGIA7v_Aegis-H8202NLB.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Aegis® H8202NLB is an unfilled, low/medium viscosity, non-lubricated nylon 6 injection molding homopolymer exhibiting excellent melt fluidity for filling thin sections. It exhibits good strength, stiffness, and toughness as well as excellent heat, chemical and abrasion resistance. |
| General Information | |
|---|---|
| Features |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.13 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (235°C/1.0 kg) | 9.8 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 1.3 | % | ASTM D955 |
| Water Absorption | ASTM D570 | ||
| 24 hr | 1.6 | % | |
| Saturation | 9.5 | % | |
| Equilibrium | 2.7 | % | |
| Extractables 1 | < 0.8 | % | Internal Method |
| Moisture Content | < 0.10 | % | ASTM D6869 |
| Relative Viscosity - @ 96% SAV | 2.61 | ||
| Viscosity - FAV | 46.0 to 52.0 | ASTM D789 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 119 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 2850 | MPa | ASTM D638 |
| Tensile Strength (Yield, 23°C) | 79.0 | MPa | ASTM D638 |
| Tensile Elongation | ASTM D638 | ||
| Yield, 23°C | 4.0 | % | |
| Break, 23°C | 55 | % | |
| Flexural Modulus (23°C) | 3010 | MPa | ASTM D790 |
| Flexural Strength (23°C) | 110 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| -40°C | 50 | J/m | |
| 23°C | 60 | J/m |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 178 | °C | |
| 1.8 MPa, Unannealed | 65.0 | °C | |
| Melting Temperature | 220 | °C | ASTM D3418 |
| CLTE - Flow | 8.3E-5 | cm/cm/°C | ASTM E831 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Processing (Melt) Temp | 240 to 280 | °C | |
| Mold Temperature | 80.0 to 95.0 | °C | |
| Injection Pressure | 3.45 to 10.3 | MPa |
| Note Message | |
|---|---|
| 1 . | Test Method: SOP-702-307 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Makroblend® UT305 | Covestro - Polycarbonates | PC+PET | Makroblend® |
| Sinvicomp SGN5819 | Teknor Apex Asia Pacific PTE. LTD. | PVC, Flexible | Sinvicomp |
| NOVA ABS 770 NAT | NOVA Polymers, Inc. | ABS | NOVA ABS |
| Hostacom EKC 297T BLACK | LyondellBasell Industries | PP Copolymer | Hostacom |
| Karina COMP. PVC YELLOW. -E 600-DA-02/381-A-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |