Chemlon® MDF2 Datasheet,Nylon 6,Teknor Apex Company (Chem Polymer)-SHANGHAI SUSHENG

Message
MDF2 is a heat stabilised 30% glass fibre reinforced nylon 6 that offers good mechanical performance coupled with good surface finish.

General Information
Filler / Reinforcement	Glass fiber reinforced material, 30% filler by weight
Additive	heat stabilizer
Features	Thermal Stability Excellent appearance
Processing Method	Injection molding

Physical	Dry	Conditioned	Unit	Test Method
Density	1.37	--	g/cm³	ISO 1183
Molding Shrinkage ¹	0.70 - 1.2	--	%	Internal method
Water Absorption (Equilibrium, 23°C, 50% RH)	1.9	--	%	ISO 62

Mechanical	Dry	Conditioned	Unit	Test Method
Tensile Modulus	8500	--	MPa	ISO 527-2
Tensile Stress	180	100	MPa	ISO 527-2
Tensile Strain (Break)	4.0	7.0	%	ISO 527-2
Flexural Modulus	7500	4000	MPa	ISO 178
Flexural Stress	230	100	MPa	ISO 178

Impact	Dry	Conditioned	Unit	Test Method
Charpy Notched Impact Strength	15	--	kJ/m²	ISO 179/1eA
Charpy Unnotched Impact Strength	55	--	kJ/m²	ISO 179/1eU
Notched Izod Impact	13	--	kJ/m²	ISO 180/A

Thermal	Dry	Conditioned	Unit	Test Method
Heat Deflection Temperature
0.45 MPa, not annealed	> 200	--	°C	ISO 75-2/B
1.8 MPa, not annealed	> 200	--	°C	ISO 75-2/A

Electrical	Dry	Conditioned	Unit	Test Method
Surface Resistivity	1.0E+15	1.0E+12	ohms	IEC 60093
Volume Resistivity	1.0E+17	--	ohms·cm	IEC 60093
Dielectric Strength (3.00 mm)	11	8.0	kV/mm	IEC 60243-1
Relative Permittivity	3.80	4.20		IEC 60250
Dissipation Factor (1 MHz)	0.020	0.080		IEC 60250
Comparative Tracking Index	500	--	V	IEC 60112

Flammability	Dry	Conditioned	Unit	Test Method
Flame Rating (1.50 mm)	HB	--		UL 94
Oxygen Index	22	--	%	ISO 4589-2

Injection	Dry	Unit
Drying Temperature	80.0	°C
Drying Time	2.0	hr
Rear Temperature	240 - 280	°C
Middle Temperature	240 - 280	°C
Front Temperature	240 - 280	°C
Processing (Melt) Temp	250 - 290	°C
Mold Temperature	60.0 - 90.0	°C
Injection Rate	Fast
Back Pressure	Low
Screw Speed	Moderate

Injection instructions
No drying is necessary unless the material has been exposed to air for longer than three hours. The appearance of splash marks on the surface of mouldings indicates excessive moisture is present.

Note Message
1 .	Mould shrinkage is significantly influenced by many factors including wall thickness, gating, moulding shape and processing conditions. The range values given are determined from specimen bar mouldings of 1.5mm to 4mm wall thickness. They are provided as a guide for comparison purposes only and no guarantee should be inferred from their inclusion. (Specimens measured in the dry state, 24 hours after moulding).

Note Message

1 .

Mould shrinkage is significantly influenced by many factors including wall thickness, gating, moulding shape and processing conditions. The range values given are determined from specimen bar mouldings of 1.5mm to 4mm wall thickness. They are provided as a guide for comparison purposes only and no guarantee should be inferred from their inclusion. (Specimens measured in the dry state, 24 hours after moulding).

Category:	Nylon 6 , Polyamide 6
Manufacturer:	Teknor Apex Company (Chem Polymer)
Trademark:	Chemlon®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	bG4ziV_Chemlon-MDF2.pdf
PRICE:	Order Products email sales@su-jiao.com

Resin Grade	Manufacturer	Category	Trademark
TRIBOCOMP® PA66 GF40 TS0	EPIC Polymers	Nylon 66	TRIBOCOMP®
Grilamid® L 25H FWA black 9225	EMS-GRIVORY	Nylon 12	Grilamid®
Huaxia Shenzhou PFA DS701	Shandong Huaxia Shenzhou New Material Co., Ltd.	PFA	Huaxia Shenzhou
Osterlene® PPC-15-1.9	Osterman & Company	PP Copolymer	Osterlene®
EcoHumer BFX3091	WooSung Chemical Co., Ltd.	PBAT	EcoHumer