ISPLEN® PM 275 AW

Category:	PP Copolymer , Polypropylene Copolymer
Manufacturer:	REPSOL
Trademark:	ISPLEN®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	bFgG0N_ISPLEN-PM-275-AW.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

WECHAT

Message

Polypropylene copolymer compound, with 20% mineral fillers reinforced and medium melt flow rate.
ISPLEN® PM275 AW gives a good compromise between stiffness and impact strength, a low warpage and shrinkage behaviour. The product is high UV stabilised.

APPLICATIONS

Automotive: Interior trims and panels.

Technical pieces, in general.

General Information
Filler / Reinforcement	Mineral, 20% Filler by Weight
Additive	UV Stabilizer
Features	Good Impact Resistance Good Stiffness Low Shrinkage Low Warpage Medium Flow
Uses	Automotive Applications Automotive Interior Parts Engineering Parts

Physical	Nominal Value	Unit	Test Method
Density	1.04	g/cm³	ISO 1183
Melt Mass-Flow Rate (MFR) (230°C/2.16 kg)	15	g/10 min	ISO 1133
Molding Shrinkage ¹	1.0 to 1.1	%	ISO 2577

Mechanical	Nominal Value	Unit	Test Method
Flexural Modulus	2300	MPa	ISO 178

Impact	Nominal Value	Unit	Test Method
Charpy Notched Impact Strength			ISO 179
-20°C	4.0	kJ/m²
0°C	5.0	kJ/m²
23°C	9.0	kJ/m²
Charpy Unnotched Impact Strength			ISO 179
-20°C	70	kJ/m²
0°C	95	kJ/m²
23°C	No Break

Thermal	Nominal Value	Unit	Test Method
Heat Deflection Temperature
0.45 MPa, Unannealed	102	°C	ISO 75-2/B
1.8 MPa, Unannealed	58.0	°C	ISO 75-2/A
Vicat Softening Temperature
--	146	°C	ISO 306/A120
--	71.0	°C	ISO 306/B120

Note Message
1 .	150x100x3mm

Resin Grade	Manufacturer	Category	Trademark
TechnoDur PBT 2 FR black (9982)	TechnoCompound GmbH	PBT	TechnoDur
Vi-Chem PVC VNC67E	Vi-Chem Corporation	PVC, Flexible	Vi-Chem PVC
Trivin™ 6304	Vi-Chem Corporation	PVC, Unspecified	Trivin™
Wondel® T TR0	Nanjing Julong Engineering Plastics Co., LTD	PBT	Wondel® T
Hostacom TSOP EM5 C13018	LyondellBasell Industries	PP Copolymer	Hostacom