Pearlthane® 12T92E
| Category: | TPU-Polyester , Thermoplastic Polyurethane Elastomer (Polyester) |
| Manufacturer: | Lubrizol Advanced Materials, Inc. |
| Trademark: | Pearlthane® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | bDKFKI_Pearlthane-12T92E.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Pearlthane® 12T92E is a special polyester-based TPU, supplied in form of translucent, colourless pellets, combining hardness with excellent processability and low temperature performance. This grade has been specially designed for mechanically demanding applications where excellent mechanical properties are required, such as timing belts Pearlthane® 12T92E can be extruded into profiles, belts, tubes and film. In the case of injection moulding, this grade is only recommended for certain applications, e.g. when large, hard-to-fill mould cavities are used. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.20 | g/cm³ | ASTM D792 |
| 20°C | 1.20 | g/cm³ | ISO 2781 |
| Moisture Content | % | Internal method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Abrasion Loss | 30.0 | mm³ | ISO 4649 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore A) | 91 | ASTM D2240, ISO 868 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ASTM D412, ISO 527 | ||
| 100% strain | 8.00 | MPa | ASTM D412, ISO 527 |
| 300% strain | 16.0 | MPa | ASTM D412, ISO 527 |
| Tensile Strength (Yield) | 40.0 | MPa | ASTM D412, ISO 527 |
| Tensile Elongation (Break) | 500 | % | ASTM D412, ISO 527 |
| Tear Strength | |||
| -- 1 | 112 | kN/m | ASTM D624 |
| -- | 110 | kN/m | ISO 34-1 |
| Compression Set | ASTM D395B | ||
| 23°C, 70 hr | 26 | % | ASTM D395B |
| 70°C, 22 hr | 40 | % | ASTM D395B |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Glass Transition Temperature 2 | -40.0 | °C | ISO 11357-2 |
| Melting Temperature 3 | 183 - 193 | °C | Internal method |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 100 - 110 | °C | |
| Drying Time | 1.0 - 2.0 | hr | |
| Rear Temperature | 195 | °C | |
| Middle Temperature | 200 | °C | |
| Front Temperature | 210 | °C | |
| Nozzle Temperature | 210 | °C | |
| Mold Temperature | 35.0 | °C | |
| Screw L/D Ratio | 23.0:1.0 |
| Injection instructions |
|---|
| Closing Force: 30 tonsScrew Diameter: 30 mmMaximum Hydraulic Pressure: 210 barMould: : Plaque 120x120x2 mm |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 100 - 110 | °C | |
| Drying Time | 1.0 - 2.0 | hr | |
| Cylinder Zone 1 Temp. | 190 - 200 | °C | |
| Cylinder Zone 2 Temp. | 195 - 210 | °C | |
| Cylinder Zone 3 Temp. | 200 - 215 | °C | |
| Cylinder Zone 4 Temp. | 200 - 220 | °C | |
| Die Temperature | 190 - 210 | °C |
| Extrusion instructions |
|---|
| L/D Ratio: 25:1 to 30:1Screw Compression Ratio: 2:1 to 3:1Screw Speed: 12 to 60 rpm |
| Note Message | |
|---|---|
| 1 . | C mould |
| 2 . | 10°C /min |
| 3 . | Temperature at which MFI = 10 g/10 min @ 21.6 kg |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Hypel® PELD50/.924 | Entec Polymers | LDPE | Hypel® |
| Karina BLACK PVC COMPOUND 802D48/ 1-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| LNP™ LUBRILOY™ RF206AXH compound | SABIC Innovative Plastics | Nylon 66 | LNP™ LUBRILOY™ |
| Lucky Enpla LPC100F | Lucky Enpla Co LTD | PC | Lucky Enpla |
| Sylvin 5211-85 Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |