ASACOM™ S9500-10
| Category: | ASA , Acrylonitrile Styrene Acrylate |
| Manufacturer: | Polymer Compounders Limited |
| Trademark: | ASACOM™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | bCUzb1_ASACOM-S9500-10.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| ASACOM S9500-10 is a high gloss easy flowing injection moulding grade ASA with exceptional weathering performance. Applications include automotive exterior covers and gardening equipment. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.05 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (220°C/10.0 kg) | 22 | g/10 min | ISO 1133 |
| Molding Shrinkage | 0.40 to 0.70 | % | ISO 294-4 |
| Water Absorption | ISO 62 | ||
| Saturation, 23°C | 1.0 | % | |
| Equilibrium, 23°C, 50% RH | 0.22 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2000 | MPa | ISO 527-2/1 |
| Tensile Stress | |||
| Yield | 35.0 | MPa | ISO 527-2/50 |
| Yield, -40°C | 63.0 | MPa | ISO 527-2 |
| Yield, 80°C | 19.0 | MPa | ISO 527-2 |
| Tensile Strain | |||
| Yield | 3.6 | % | ISO 527-2/50 |
| Yield, -40°C | 3.6 | % | ISO 527-2 |
| Yield, 80°C | 2.4 | % | ISO 527-2 |
| Break | 40 | % | ISO 527-2 |
| Flexural Stress | 58.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 22 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 150 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact Strength (23°C) | 16 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 90.0 | °C | ISO 75-2/Be |
| 1.8 MPa, Unannealed | 79.0 | °C | ISO 75-2/Ae |
| Vicat Softening Temperature | 90.0 | °C | ISO 306/B50 |
| CLTE - Flow | 9.0E-5 | cm/cm/°C | ISO 11359-2 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.800 mm | HB | ||
| 1.50 mm | HB |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Processing (Melt) Temp | 240 | °C | |
| Mold Temperature | 60.0 | °C | |
| Injection Velocity | 60 | mm/sec |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Michimid K4220 | API Polymers, Inc. | Nylon 66 | Michimid |
| ULTEM™ HU2100 resin | SABIC Innovative Plastics | PEI | ULTEM™ |
| Fainplast PVC FKA 92 | Fainplast Compounds S.r.l | PVC, Unspecified | Fainplast PVC |
| Braskem EVA HM728F | Braskem | EVA | Braskem EVA |
| Durethan® BG 30 X W1 000000 | LANXESS GmbH | Nylon 6 | Durethan® |