Lupoy® GP5008A
| Category: | PC+ABS , Polycarbonate + ABS |
| Manufacturer: | LG Chem Ltd. |
| Trademark: | Lupoy® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | bBQmog_Lupoy-GP5008A.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Description General Purpose, High Flow Application Miscellaneous Goods |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Forms |
|
| Processing Method |
|
| Multi-Point Data |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.10 | g/cm³ | ASTM D792 |
| -- | 1060 | kg/m³ | ISO 1183 1 |
| Melt Mass-Flow Rate (MFR) | 2.0 | g/10 min | ASTM D1238 |
| Melt volume-flow rate (260°C/5.0 kg) | 18.0 | cm³/10min | ISO 1133 2 |
| Molding Shrinkage - Flow | 0.50 to 0.80 | % | ASTM D955 |
| Water Absorption (Saturation) | 0.16 | % | ISO 62 3 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile modulus | 1600 | MPa | ISO 527-2 4 |
| Tensile Strength | |||
| Yield, 3.20 mm 5 | 39.2 | MPa | ASTM D638 |
| Yield | 36.0 | MPa | ISO 527-2 6 |
| Tensile Strain (Yield) | 3.7 | % | ISO 527-2 7 |
| Nominal strain at break | 27 | % | ISO 527-2 8 |
| Flexural Modulus 9(3.20 mm) | 1670 | MPa | ASTM D790 |
| Flexural Strength 10(3.20 mm) | 59.8 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy notched impact strength (23°C) | 35.3 | kJ/m² | ISO 179/1eA 11 |
| Charpy impact strength | ISO 179/1eU 12 | ||
| -30°C | No Break | ||
| 23°C | No Break | ||
| Notched Izod Impact (23°C, 3.20 mm) | 450 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, Unannealed, 6.40 mm | 91.0 | °C | ASTM D648 |
| 1.8 MPa | 84.0 | °C | ISO 75-2 13 |
| Glass Transition Temperature 14 | 140 | °C | ISO 11357-2 15 |
| Vicat Softening Temperature (50°C/h, B (50N)) | 97.7 | °C | ISO 306 16 |
| CLTE | ISO 11359-2 17 | ||
| Flow | 1.1E-4 | cm/cm/°C | |
| Transverse | 1.1E-4 | cm/cm/°C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface resistivity | 7.5E+14 | ohms | IEC 60093 18 |
| Volume resistivity | > 1.0E+13 | ohms·m | IEC 60093 19 |
| Electric strength | 43 | kV/mm | IEC 60243-1 20 |
| Relative Permittivity (1 MHz) | 2.70 | IEC 60250 21 | |
| Dissipation Factor (1 MHz) | 0.010 | IEC 60250 22 | |
| Comparative tracking index | 275 | IEC 60112 23 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 to 90.0 | °C | |
| Drying Time | 4.0 to 6.0 | hr | |
| Suggested Max Moisture | < 0.020 | % | |
| Rear Temperature | 230 to 250 | °C | |
| Middle Temperature | 235 to 255 | °C | |
| Front Temperature | 235 to 255 | °C | |
| Nozzle Temperature | 235 to 255 | °C | |
| Processing (Melt) Temp | 235 to 250 | °C | |
| Mold Temperature | 50.0 to 70.0 | °C | |
| Screw Speed | 40 to 70 | rpm |
| Note Message | |
|---|---|
| 1 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 2 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 3 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 4 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 5 . | 50 mm/min |
| 6 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 7 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 8 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 9 . | 10 mm/min |
| 10 . | 10 mm/min |
| 11 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 12 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 13 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 14 . | 10 °C/min |
| 15 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 16 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 17 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 18 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 19 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 20 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 21 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 22 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 23 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| UNITAL® LZU | Nytef Plastics, Ltd. | Acetal (POM) Copolymer | UNITAL® |
| Axiall PVC 8880 | Axiall Corporation | PVC, Flexible | Axiall PVC |
| Escorene™ Ultra UL 00514 | ExxonMobil Chemical | EVA | Escorene™ Ultra |
| Plasmer 5030N/1002 | HYUNDAI EP Co., Ltd. | TPE | Plasmer |
| LUVOCOM® 1105/CF/10/GR/10/TF/10-2 Axial. | LEHVOSS Group | PEEK | LUVOCOM® |