NYCOA Polyamide 715 C
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Nycoa (Nylon Corporation of America) |
| Trademark: | NYCOA Polyamide |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | bAgHHO_NYCOA-Polyamide-715-C.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
NYCOA 715 C is an unextracted, high viscosity Nylon 6 resin for extrusion processing. The high viscosity of the resin makes it suitable for complex profile extrusion, mandrel extrusion as well as for blow molding applications. NYCOA 715 C is available with custom additive packages: heat stabilizer, UV stabilizer, flame retardant and/or custom colors. Typical applications include profile extrusion, flexible tubing, and mandrels. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.13 | g/cm³ | ASTM D792 |
| Water Absorption (24 hr) | 2.0 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1 | 57.2 | MPa | ASTM D638 |
| Tensile Elongation 2(Break) | 300 | % | ASTM D638 |
| Flexural Modulus 3 | 862 | MPa | ASTM D790 |
| Flexural Strength 4 | 37.2 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (6.35 mm) | 170 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed) | 163 | °C | ASTM D648 |
| Melting Temperature | 221 | °C | DSC |
| Additional Information |
|---|
| Relative Viscosity, NYCOA Method: 4.5 to 5.3 SAVWater Extractable, NYCOA Method: 8 to 10 %Tensile Elongation at Break, ASTM D638, 2 in/min: 300+%The value listed as Melting Point DSC, was tested in accordance with ASTM D789. |
| Note Message | |
|---|---|
| 1 . | 51 mm/min |
| 2 . | 51 mm/min |
| 3 . | 51 mm/min |
| 4 . | 51 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 1309 | RTP Company | PPS | RTP |
| Thanelene® TPU S80A15 PRTA010 TP305 MSP | Petropol Industry and Trade of Polymers LTDA | TPU-Polyester | Thanelene® TPU |
| TRANSMARE® 9RCGF30-1.001 | Transmare Compounding B.V. | PP Homopolymer | TRANSMARE® |
| Optix® CP-924 | Plaskolite West, Inc. | Acrylic (PMMA) | Optix® |
| Ultramid® Structure B3WG12 LFX BK23215 | BASF Corporation | Nylon 6 | Ultramid® |