Ebalta GM 984-2 / Comp. A+B

Category:	PUR, Unspecified , Polyurethane
Manufacturer:	Ebalta Kunststoff GmbH
Trademark:	Ebalta
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	b9vwxd_Ebalta-GM-984-2-Comp-A-B.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

Message
This product is a polyurethane system. GM 984-1 Comp. B (Amine) can be subject to colour variations due to raw materials, but these colour variations have no influence on the quality and the properties of the product. The postcured material is not UV stable and darkens by and by. However according to our experience the change in colour does not affect its utilizability. Physical final properties will be achieved after 7 days' curing at room temperature or after postcuring for 8 hrs. at 80°C. As bonding agent on aluminium support we recommend our PU coupling paste KP 8. Applications Core boxes fixtures Properties non-toxic according to regulations for hazardous material very abrasion resistant hard flexible no brittleness phase very well castable Shore D hardness approx. 67

Message

This product is a polyurethane system.
GM 984-1 Comp. B (Amine) can be subject to colour variations due to raw materials, but these colour variations have no influence on the quality and the properties of the product.
The postcured material is not UV stable and darkens by and by. However according to our experience the change in colour does not affect its utilizability.
Physical final properties will be achieved after 7 days' curing at room temperature or after postcuring for 8 hrs. at 80°C.
As bonding agent on aluminium support we recommend our PU coupling paste KP 8.

Applications

Core boxes

fixtures

Properties

non-toxic according to regulations for hazardous material

very abrasion resistant

hard flexible

no brittleness phase

very well castable

Shore D hardness approx. 67

General Information
Features	Semi Rigid Good flexibility Good wear resistance Non-toxic
Appearance	Orange
Processing Method	Casting

Hardness	Nominal Value		Test Method
Durometer Hardness (Shore D)	65 - 69		ISO 7619

Mechanical	Nominal Value	Unit	Test Method
Tensile Stress	26.0 - 30.0	MPa	ISO 527-2
Tensile Strain (Break)	200 - 240	%	ISO 527-2
Flexural Modulus	785 - 865	MPa	ISO 178
Flexural Stress	30.0 - 32.0	MPa	ISO 178
Flexural Strain at Flexural Strength	6.5 - 7.5	%	ISO 178

Thermoset	Nominal Value	Unit
Thermoset Components
Resin	Mixing ratio by weight: 100
Hardening method	Mixing ratio by weight: 130

Additional Information
Wear jet test : 40 W(V/t) [mm³/min] (internal tests)

Uncured Properties	Nominal Value	Unit
Density (20°C)	1.13 - 1.17	g/cm³
Viscosity (25°C)	2.3 - 3.1	Pa·s
Curing Time (20°C)	12 - 16	hr
Pot Life ¹(20°C)	17 - 20	min

Note Message
1 .	200 g

Resin Grade	Manufacturer	Category	Trademark
POLYNIL® C50L	Nilit Plastics	Nylon 66/6	POLYNIL®
RTP 1005 HI FR A	RTP Company	PBT	RTP
Tenac™-C MT754	Asahi Kasei Chemicals Corporation	Acetal (POM) Copolymer	Tenac™-C
Gallonprene® GP520-7502	Shenzhen Sungallon Rubber & Plastic Corporation Limited	TPE	Gallonprene®
EQUATE PE EMDA-6147	EQUATE Petrochemical Company KSCC	HDPE Copolymer	EQUATE PE