REPRO ABS RE6
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | Rondo Plast AB |
| Trademark: | REPRO |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | b9ncaa_REPRO-ABS-RE6.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Injection moulding, high impact |
| General Information | |
|---|---|
| Recycled Content |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.05 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) | ISO 1133 | ||
| 220°C/10.0 kg | 16 | g/10 min | |
| 230°C/5.0 kg | 8.0 | g/10 min | |
| Molding Shrinkage | ISO 2577 | ||
| Across Flow | 0.60 to 0.80 | % | |
| Flow | 0.60 to 0.80 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | 35.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 30 | % | ISO 527-2 |
| Flexural Modulus (23°C) | 2100 | MPa | ISO 178 |
| Flexural Stress | 65.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | ||
| -20°C | 8.0 | kJ/m² | |
| 23°C | 14 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 92.0 | °C | ISO 306/B50 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.60 mm) | HB | UL 94 | |
| Glow Wire Ignition Temperature (2.00 mm) | 650 | °C | IEC 60695-2-13 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Processing (Melt) Temp | 190 to 230 | °C | |
| Mold Temperature | 60.0 to 80.0 | °C | |
| Injection Pressure | 90.0 to 150 | MPa | |
| Injection Rate | Fast | ||
| Back Pressure | 1.00 to 1.50 | MPa |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Axiall PVC 10703 | Axiall Corporation | PVC, Flexible | Axiall PVC |
| GAPEX® RPP10EA53BK | Ferro Corporation | PP Homopolymer | GAPEX® |
| Globalprene® 3545 | Lee Chang Yung Chemical Industry Corp. | SBS | Globalprene® |
| Hostacom X M3 V02 | LyondellBasell Industries | PP Copolymer | Hostacom |
| PENTAMID A GV25 H green 6032/1 | PENTAC Polymer GmbH | Nylon 66 | PENTAMID A |