Durethan® BTC 65 H3.0 EF 901510
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | LANXESS GmbH |
| Trademark: | Durethan® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | b7sLE1_Durethan-BTC-65-H3-0-EF-901510.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PA 6, 65% mineral, injection molding, improved heat conductivity |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 2.01 | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 2577 | ||
| Across Flow : 280°C, 2.00 mm 1 | 0.68 | % | |
| Across Flow : 120°C, 4 hr, 2.00 mm 2 | 0.18 | % | |
| Flow : 280°C, 2.00 mm 3 | 0.66 | % | |
| Flow : 120°C, 4 hr, 2.00 mm 4 | 0.16 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 9900 | MPa | ISO 527-2/1 |
| Tensile Stress (Break, 23°C) | 90.0 | MPa | ISO 527-2/5 |
| Tensile Strain (Break, 23°C) | 3.0 | % | ISO 527-2/5 |
| Nominal Tensile Strain at Break (23°C) | 3.0 | % | ISO 527-2/50 |
| Flexural Modulus 5(23°C) | 10600 | MPa | ISO 178/A |
| Flexural Stress 6(23°C) | 160 | MPa | ISO 178/A |
| Flexural Strain at Flexural Strength 7(23°C) | 3.0 | % | ISO 178/A |
| Additional Information | Nominal Value | Test Method | |
|---|---|---|---|
| ISO Shortname | PA6, GHR, 10-090, MD65 | ISO 1874 |
| Injection | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Residual Moisture Content | 0.030 to 0.12 | % | Karl Fisher |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength (23°C) | < 10 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength (23°C) | 35 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melting Temperature 8 | 221 | °C | ISO 11357-3 |
| Thermal Conductivity 9 | 1.0 | W/m/K | ISO 22007-4 |
| Injection | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Drying Temperature - Dry Air Dryer | 80.0 | °C | |
| Drying Time - Dry Air Dryer | 2.0 to 6.0 | hr | |
| Processing (Melt) Temp | 280 to 300 | °C | |
| Mold Temperature | 80.0 to 120 | °C |
| Note Message | |
|---|---|
| 1 . | 60x60x2mm, 80°C MT, 600 bar |
| 2 . | 60x60x2mm |
| 3 . | 60x60x2mm, 80°C MT, 600 bar |
| 4 . | 60x60x2mm |
| 5 . | 2.0 mm/min |
| 6 . | 2.0 mm/min |
| 7 . | 2 mm/min |
| 8 . | 10°C/min |
| 9 . | Through-plane |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Moplen RP348R | LyondellBasell Industries | PP Random Copolymer | Moplen |
| AKROMID® B3 GFM 10/20 1 grey (4561) | AKRO-PLASTIC GmbH | Nylon 6 | AKROMID® |
| Delta PPO FR1G21 | Delta Polymers | PPE+PS | Delta |
| LNP™ STAT-KON™ DX05042 compound | SABIC Innovative Plastics Europe | PC | LNP™ STAT-KON™ |
| Sylvin 9067-70 Grey 9505 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |