INSULCAST® 136/INSULCURE 11B
| Category: | Epoxy , Epoxy; Epoxide |
| Manufacturer: | ITW Polymers Coatings North America |
| Trademark: | INSULCAST® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | b7r0kS_INSULCAST-136-INSULCURE-11B.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| INSULCAST 136 is an easy to use epoxy casting/potting compound exhibiting excellent adhesion to metals, ceramics and most plastics. When properly cured with INSULCURE 11B, INSULCAST 136 will conform to the requirements of MIL-I-16923, Types B, C & D, and will not support fungus growth. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Processing Method |
|
| Hardness | Nominal Value | Test Method | |
|---|---|---|---|
| Durometer Hardness (Shore D) | 89 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 70.3 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 2.0 to 4.0 | % | ASTM D638 |
| Flexural Strength | 117 | MPa | ASTM D790 |
| Compressive Strength | 107 | MPa | ASTM D695 |
| Thermal | Nominal Value | Unit | |
|---|---|---|---|
| CLTE - Flow | 4.0E-5 | cm/cm/°C | |
| Thermal Conductivity | 0.72 | W/m/K | |
| Heat Deflection Temperature | 155 | °C | |
| Service Temperature | 155 | °C |
| Cured Properties | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Linear Shrinkage | 0.20 | % |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 5.0E+16 | ohms·cm | ASTM D257 |
| Dielectric Strength | 17 | kV/mm | ASTM D149 |
| Dielectric Constant (1 kHz) | 4.80 | ASTM D150 | |
| Dissipation Factor (1 kHz) | 0.020 | ASTM D150 |
| Thermoset | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Thermoset Components | |||
| Hardener | Mix Ratio by Weight: 9.0 to 10 | ||
| Resin | Mix Ratio by Weight: 100 | ||
| Shelf Life | 52 | wk | |
| Post Cure Time (150°C) | 1.0 | hr |
| Uncured Properties | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Color | |||
| -- 1 | Amber | ||
| -- 2 | Black | ||
| Density | |||
| -- 3 | 0.948 | g/cm³ | |
| -- 4 | 1.59 | g/cm³ | |
| Viscosity | ASTM D2393 | ||
| -- 5 | 0.70 | Pa·s | |
| -- 6 | 25 | Pa·s | |
| -- 7 | 80 | Pa·s | |
| Curing Time (100°C) | 2.0 | hr | |
| Pot Life (25°C) | 150 | min |
| Note Message | |
|---|---|
| 1 . | INSULCURE 11B |
| 2 . | INSULCAST 136 |
| 3 . | INSULCURE 11B |
| 4 . | INSULCAST 136 |
| 5 . | INSULCURE 11B |
| 6 . | Mixed |
| 7 . | INSULCAST 136 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sumikon® PM-9625 | Sumitomo Bakelite Co., Ltd. | Phenolic | Sumikon® |
| Karina PVC COMPOUND WHITE COLOR - E-800-10/1-A-ERYB-PO | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Lucent PP GPP-330 | Lucent Polymers, Inc. | PP, Unspecified | Lucent PP |
| TAFMER™ DF810 | Mitsui Chemicals, Inc. | PAO | TAFMER™ |
| UNITIKA Nylon 6 RUN35-TA | UNITIKA Plastics Division | Nylon 6 | UNITIKA Nylon 6 |