Ryton® R-7-121BL
| Category: | PPS , Polyphenylene Sulfide |
| Manufacturer: | Solvay Specialty Polymers |
| Trademark: | Ryton® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | b7lacy_Ryton-R-7-121BL.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Ryton® R-7-121NA and R-7-121BL glass fiber and mineral filled polyphenylene sulfide compounds provide good mechanical strength with good flow and low maintenance molding using conventional molding equipment. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.95 | g/cm³ | ASTM D792 |
| Molding Shrinkage | |||
| Flow : 3.20 mm | 0.20 | % | |
| Across Flow : 3.20 mm | 0.40 | % | |
| Water Absorption (23°C, 24 hr) | 0.020 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness | ASTM D785 | ||
| M-Scale | 101 | ||
| R-Scale | 118 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | |||
| -- | 117 | MPa | ASTM D638 |
| -- | 125 | MPa | ISO 527-2 |
| Tensile Elongation (Break) | 0.90 | % | ASTM D638, ISO 527-2 |
| Flexural Modulus | |||
| -- | 17200 | MPa | ASTM D790 |
| -- | 18000 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 200 | MPa | ASTM D790 |
| -- | 195 | MPa | ISO 178 |
| Compressive Strength | 285 | MPa | ASTM D695 |
| Poisson's Ratio | 0.36 | ISO 527 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 3.18 mm | 53 | J/m | ASTM D256 |
| -- | 6.0 | kJ/m² | ISO 180/A |
| Unnotched Izod Impact | |||
| 3.18 mm | 210 | J/m | ASTM D4812 |
| -- | 14 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 265 | °C | ASTM D648 |
| CLTE | ASTM E831 | ||
| Flow : -50 to 50°C | 1.5E-5 | cm/cm/°C | |
| Flow : 100 to 200°C | 1.5E-5 | cm/cm/°C | |
| Transverse : -50 to 50°C | 3.0E-5 | cm/cm/°C | |
| Transverse : 100 to 200°C | 7.0E-5 | cm/cm/°C | |
| Thermal Conductivity | 0.58 | W/m/K | |
| UL Temperature Rating | 220 to 240 | °C | UL 746B |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+16 | ohms | ASTM D257 |
| Volume Resistivity | 1.0E+15 | ohms·cm | ASTM D257 |
| Dielectric Strength | 18 | kV/mm | ASTM D149 |
| Dielectric Constant | ASTM D150 | ||
| 25°C, 1 kHz | 4.80 | ||
| 25°C, 1 MHz | 4.90 | ||
| Dissipation Factor | ASTM D150 | ||
| 25°C, 1 kHz | 4.0E-3 | ||
| 25°C, 1 MHz | 2.0E-3 | ||
| Arc Resistance | 185 | sec | ASTM D495 |
| Comparative Tracking Index (CTI) | 250 | V | UL 746 |
| Insulation Resistance 1(90°C) | 1.0E+11 | ohms |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.60 mm) | V-0 5VA | UL 94 | |
| Oxygen Index | 61 | % | ASTM D2863 |
| Note Message | |
|---|---|
| 1 . | 95%RH, 48 hr |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Texin® 945 U | Covestro - PUR | TPU-Polyether | Texin® |
| TOTAL Polystyrene Impact 7240 | TOTAL Refining & Chemicals | PS (HIPS) | TOTAL Polystyrene |
| Karina WHITE PVC COMPOUND 750D10/ 1-DY-AC | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Plaslube® AC-80/TF/15 | Techmer Engineered Solutions | Acetal (POM) Copolymer | Plaslube® |
| Sylvin 83020-80UV White 1579 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |