Miramid® SK2515CW black

Category:	Nylon 66 , Polyamide 66
Manufacturer:	BASF Leuna GmbH
Trademark:	Miramid®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	b7YR2Z_Miramid-SK2515CW-black.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

WECHAT

Message

Miramid® SK2515CW black is a Polyamide 66 (Nylon 66) material filled with 15% glass fiber and 25% mineral. It is available in Europe for injection molding.

Important attributes of Miramid® SK2515CW black are:

Flame Rated

Chemical Resistant

Crystalline

Good Stiffness

Typical applications include:

Automotive

Engineering/Industrial Parts

Housings

General Information
Filler / Reinforcement	Glass Fiber, 15% Filler by Weight Mineral, 25% Filler by Weight
Features	Crystalline Fuel Resistant Good Flow Good Stiffness Grease Resistant Oil Resistant Solvent Resistant
Uses	Automotive Exterior Trim Automotive Under the Hood Electric Motor Housings Engineering Parts Wheels
Appearance	Black
Forms	Granules
Processing Method	Injection Molding

Physical	Dry	Conditioned	Unit	Test Method
Density	1460	--	kg/m³	ISO 1183 ¹
Water Absorption				ISO 62 ²
Saturation	5.0	--	%
Equilibrium	1.5	--	%
Viscosity number	140	--	cm³/g	ISO 307, 1157, 1628 ³

Hardness	Dry	Conditioned	Unit	Test Method
Ball Indentation Hardness	260	--	MPa	ISO 2039-1

Mechanical	Dry	Conditioned	Unit	Test Method
Tensile modulus	8400	5000	MPa	ISO 527-2 ⁴
Tensile Stress (Break)	140	80.0	MPa	ISO 527-2 ⁵
Tensile Strain (Break)	2.5	6.0	%	ISO 527-2 ⁶
Flexural Stress ⁷	200	140	MPa	ISO 178

Impact	Dry	Conditioned	Unit	Test Method
Charpy notched impact strength				ISO 179/1eA ⁸
-30°C	3.00	--	kJ/m²
23°C	3.00	5.00	kJ/m²
Charpy impact strength				ISO 179/1eU ⁹
-30°C	40.0	--	kJ/m²
23°C	40.0	45.0	kJ/m²

Thermal	Dry	Conditioned	Unit	Test Method
Deflection Temperature Under Load				ISO 75-2 ¹⁰
0.45 MPa	250	--	°C
1.8 MPa	240	--	°C
Melting Temperature (DSC)	260	--	°C	ISO 3146

Electrical	Dry	Conditioned	Unit	Test Method
Volume resistivity	1.0E+13	1.0E+10	ohms·m	IEC 60093 ¹¹
Dissipation Factor (1 MHz)	0.020	0.15		IEC 60250 ¹²

Flammability	Dry	Conditioned	Unit	Test Method
Burning Rate (1.00 mm)	< 100	--	mm/min	FMVSS 302
Flame Rating (1.50 mm)	HB	--		UL 94
Burning Behav. at thickness h (1.50 mm)	HB	--		ISO 1210 ¹³
Glow Wire Flammability Index (1.00 mm)	650	--	°C	IEC 60695-2-12

Injection	Dry	Unit
Processing (Melt) Temp	260 to 290	°C
Mold Temperature	80.0 to 120	°C

Note Message
1 .	Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted.
2 .	Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted.
3 .	Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted.
4 .	Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted.
5 .	Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted.
6 .	Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted.
7 .	Typical values for uncoloured product at 23°C and 50% relative humidity
8 .	Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted.
9 .	Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted.
10 .	Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted.
11 .	Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted.
12 .	Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted.
13 .	Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted.

Resin Grade	Manufacturer	Category	Trademark
RTP 100 HS	RTP Company	PP, Unspecified	RTP
Texalan® 5 Series 564D	Austin Novel Materials Co. Ltd.	TPU-Polyester	Texalan® 5 Series
TOTAL Polypropylene PPR 3727W	TOTAL Refining & Chemicals	PP Random Copolymer	TOTAL Polypropylene
AKROLOY® PA GF 50 black (2706)	AKRO-PLASTIC GmbH	Nylon 66+Nylon 6I/6T	AKROLOY®
Kumho EP HSP 8344	Korea Kumho Petrochemical Co., Ltd.	PPE+PS	Kumho EP