Badamid® B70 GF30
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Bada AG |
| Trademark: | Badamid® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | b4FoNW_Badamid-B70-GF30.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Polyamide 6 injection moulding standard grade with 30% of glass fibre reinforcement. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.35 | -- | g/cm³ | ISO 1183 |
| Water Absorption | ISO 62 | |||
| Saturation, 23°C | 6.7 | -- | % | |
| Equilibrium, 23°C, 50% RH | 2.1 | -- | % |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus (23°C) | 9350 | 6200 | MPa | ISO 527-2/1 |
| Tensile Stress 1(Break, 23°C) | 175 | 110 | MPa | ISO 527-2/5 |
| Tensile Strain 2(Break, 23°C) | 3.5 | 5.5 | % | ISO 527-2/5 |
| Flexural Stress 3(23°C) | 245 | 200 | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength 4 | ISO 179/1eA | |||
| -30°C | 14 | -- | kJ/m² | |
| 23°C | 15 | 24 | kJ/m² | |
| Charpy Unnotched Impact Strength 5 | ISO 179/1eU | |||
| -30°C | 80 | -- | kJ/m² | |
| 23°C | 90 | 110 | kJ/m² | |
| Notched Izod Impact Strength 6 | ISO 180/1A | |||
| -30°C | 12 | -- | kJ/m² | |
| 23°C | 15 | 20 | kJ/m² |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature 7 | ||||
| 0.45 MPa, Unannealed | 220 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 210 | -- | °C | ISO 75-2/A |
| Melting Temperature (DSC) 8 | 222 | -- | °C | ISO 3146 |
| CLTE | DIN 53752 | |||
| Flow | 2.0E-5 | -- | cm/cm/°C | |
| Transverse | 6.2E-5 | -- | cm/cm/°C | |
| Maximum Service Temperature | IEC 216 | |||
| 20000 hrs | 110 | -- | °C | |
| some hours | 200 | -- | °C |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity 9 | 1.0E+12 | 1.0E+10 | ohms | IEC 60093 |
| Volume Resistivity 10 | 1.0E+15 | 1.0E+12 | ohms·cm | IEC 60093 |
| Relative Permittivity 11 | 3.80 | 6.80 | IEC 60250 | |
| Dissipation Factor (1 MHz) | 0.023 | 0.22 | IEC 60250 | |
| Comparative Tracking Index | 500 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating | UL 94 | |||
| 0.800 mm 12 | HB | -- | ||
| 1.60 mm 13 | HB | -- |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Processing (Melt) Temp | 260 to 280 | °C | |
| Mold Temperature | 80.0 to 90.0 | °C |
| Note Message | |
|---|---|
| 1 . | Test Specimen accordng to ISO 3167, Type A |
| 2 . | Test Specimen accordng to ISO 3167, Type A |
| 3 . | 80x10x4 mm |
| 4 . | 80x10x4 mm |
| 5 . | 80x10x4 mm |
| 6 . | 80x10x4 mm |
| 7 . | 110x10x4 mm |
| 8 . | 10 K/min, Compound for moulding |
| 9 . | 80x80x1 mm |
| 10 . | 80x80x1 mm |
| 11 . | 80x80x1 mm |
| 12 . | 125x13x0.8 mm |
| 13 . | 125x13x1.6 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sinpolene CFN3088 | Teknor Apex Asia Pacific PTE. LTD. | LDPE+LLDPE | Sinpolene |
| TRIREX® Compound 3025AS | Samyang Corporation | PC | TRIREX® Compound |
| VALOX™ V4760 resin | SABIC Innovative Plastics Asia Pacific | PBT | VALOX™ |
| Ecomass® 1050ZB92 | Ecomass Technologies | Nylon 12 | Ecomass® |
| Iupilon® EFR3000 | Mitsubishi Engineering-Plastics Corp | PC | Iupilon® |