XENOY™ 6620U resin
| Category: | PC+PBT , Polycarbonate + PBT |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | XENOY™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | b2TOwA_XENOY-6620U-resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PBT+PC, Unfilled, Impact Modified, UV stabilized. Outstanding low temperature impact performance and chemical resistance. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.20 | g/cm³ | ASTM D792 |
| -- | 1.21 | g/cm³ | ISO 1183 |
| Specific Volume | 0.835 | cm³/g | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (266°C/5.0 kg) | 22 | g/10 min | ASTM D1238 |
| Melt Volume-Flow Rate (MVR) (265°C/5.0 kg) | 17.1 | cm³/10min | ISO 1133 |
| Molding Shrinkage | Internal Method | ||
| Flow : 3.20 mm | 1.6 to 1.8 | % | |
| Across Flow : 3.20 mm | 1.6 to 1.8 | % | |
| Water Absorption (Saturation, 23°C) | 0.14 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 1780 | MPa | ASTM D638 |
| -- | 1830 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 2 | 43.7 | MPa | ASTM D638 |
| Yield | 41.1 | MPa | ISO 527-2/50 |
| Break 3 | 32.9 | MPa | ASTM D638 |
| Break | 31.7 | MPa | ISO 527-2/50 |
| Tensile Elongation | |||
| Yield 4 | 4.2 | % | ASTM D638 |
| Yield | 3.9 | % | ISO 527-2/50 |
| Break 5 | 150 | % | ASTM D638 |
| Break | 19 | % | ISO 527-2/50 |
| Flexural Modulus | |||
| 50.0 mm Span 6 | 1780 | MPa | ASTM D790 |
| -- 7 | 1700 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 60.0 | MPa | ISO 178 |
| Yield, 50.0 mm Span 8 | 63.6 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 9(23°C) | 72 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact | |||
| -30°C | 670 | J/m | ASTM D256 |
| 23°C | 900 | J/m | ASTM D256 |
| -30°C 10 | 51 | kJ/m² | ISO 180/1A |
| 23°C 11 | 54 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact (23°C) | 1600 | J/m | ASTM D4812 |
| Instrumented Dart Impact (23°C, Total Energy) | 56.3 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 6.40 mm | 98.9 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 6.40 mm | 60.0 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 12 | 50.5 | °C | ISO 75-2/Af |
| Vicat Softening Temperature | |||
| -- | 123 | °C | ASTM D1525 13 |
| -- | 119 | °C | ISO 306/B50 |
| -- | 122 | °C | ISO 306/B120 |
| CLTE | ASTM E831, ISO 11359-2 | ||
| Flow : -40 to 40°C | 9.9E-5 | cm/cm/°C | |
| Transverse : -40 to 40°C | 1.0E-4 | cm/cm/°C | |
| RTI Elec | 75.0 | °C | UL 746 |
| RTI Imp | 75.0 | °C | UL 746 |
| RTI Str | 75.0 | °C | UL 746 |
| Electrical | Nominal Value | Test Method | |
|---|---|---|---|
| Arc Resistance 14 | PLC 5 | ASTM D495 | |
| Comparative Tracking Index (CTI) | PLC 0 | UL 746 | |
| High Amp Arc Ignition (HAI) | PLC 0 | UL 746 | |
| High Voltage Arc Tracking Rate (HVTR) | PLC 1 | UL 746 | |
| Hot-wire Ignition (HWI) | PLC 3 | UL 746 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.47 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 104 to 116 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Drying Time, Maximum | 6.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Suggested Shot Size | 50 to 80 | % | |
| Rear Temperature | 232 to 246 | °C | |
| Middle Temperature | 241 to 254 | °C | |
| Front Temperature | 249 to 266 | °C | |
| Nozzle Temperature | 249 to 271 | °C | |
| Processing (Melt) Temp | 249 to 271 | °C | |
| Mold Temperature | 37.8 to 82.2 | °C | |
| Back Pressure | 0.172 to 0.345 | MPa | |
| Vent Depth | 0.013 to 0.020 | mm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | Type I, 50 mm/min |
| 3 . | Type I, 50 mm/min |
| 4 . | Type I, 50 mm/min |
| 5 . | Type I, 50 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 2.0 mm/min |
| 8 . | 1.3 mm/min |
| 9 . | 80*10*4 sp=62mm |
| 10 . | 80*10*4 |
| 11 . | 80*10*4 |
| 12 . | 80*10*4 mm |
| 13 . | Rate B (120°C/h), Loading 2 (50 N) |
| 14 . | Tungsten Electrode |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| ResMart Ultra PBT 23 | ResMart | PBT | ResMart Ultra |
| Shinko-Lac® ASA E310 | Mitsubishi Rayon America Inc. | ASA | Shinko-Lac® |
| VITAMIDE® BK40BK6440 | Jackdaw Polymers | Nylon 6 | VITAMIDE® |
| Evermore PUR SW-3145 | Evermore Chemical Industry Co., Ltd. | PUR, Unspecified | Evermore PUR |
| KOCETAL® TC701 | Kolon Plastics, Inc. | Acetal (POM) Copolymer | KOCETAL® |