Iupilon® FPR3500
| Category: | PC , Polycarbonate |
| Manufacturer: | Mitsubishi Engineering-Plastics Corp |
| Trademark: | Iupilon® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | b1xpen_Iupilon-FPR3500.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Iupilon® FPR3500 is a Polycarbonate (PC) material. It is available in Asia Pacific, Europe, or North America for injection molding. Important attributes of Iupilon® FPR3500 are:
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.19 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (300°C/1.2 kg) | 18 | g/10 min | ISO 1133 |
| Melt Volume-Flow Rate (MVR) (300°C/1.2 kg) | 17.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage | |||
| Across Flow : 3.20 mm | 0.30 to 0.50 | % | |
| Flow : 3.20 mm | 0.30 to 0.50 | % | |
| Water Absorption (Saturation, 23°C) | 0.24 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2500 | MPa | ISO 527-2 |
| Tensile Stress (Yield) | 63.0 | MPa | ISO 527-2 |
| Tensile Strain (Yield) | 4.4 | % | ISO 527-2 |
| Nominal Tensile Strain at Break | 81 | % | ISO 527-2 |
| Flexural Modulus | 2700 | MPa | ISO 178 |
| Flexural Stress | 98.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 50 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength (23°C) | No Break | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 107 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 97.0 | °C | ISO 75-2/A |
| CLTE | ISO 11359-2 | ||
| Flow | 6.6E-5 | cm/cm/°C | |
| Transverse | 6.7E-5 | cm/cm/°C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 4.0E+15 | ohms | IEC 60093 |
| Volume Resistivity | 2.0E+16 | ohms·cm | IEC 60093 |
| Electric Strength | IEC 60243-1 | ||
| 1.00 mm | 31 | kV/mm | |
| 3.00 mm | 18 | kV/mm | |
| Relative Permittivity | IEC 60250 | ||
| 100 Hz | 3.10 | ||
| 1 MHz | 3.10 | ||
| Dissipation Factor | IEC 60250 | ||
| 100 Hz | 3.4E-3 | ||
| 1 MHz | 7.1E-3 | ||
| Comparative Tracking Index (CTI) | PLC 2 | UL 746 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.380 mm | V-2 | ||
| 0.750 mm | V-0 | ||
| 2.00 mm | 5VB |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 to 90.0 | °C | |
| Drying Time | 4.0 to 8.0 | hr | |
| Rear Temperature | 230 to 280 | °C | |
| Middle Temperature | 240 to 290 | °C | |
| Front Temperature | 250 to 300 | °C | |
| Nozzle Temperature | 250 to 300 | °C | |
| Mold Temperature | 60.0 to 90.0 | °C | |
| Injection Pressure | 50.0 to 200 | MPa | |
| Screw Speed | 50 to 150 | rpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP ESD C 204 | RTP Company | Nylon 66 | RTP |
| Ming Dih EPS LS3 | Ming Dih Group Corporation | PS (EPS) | Ming Dih EPS |
| LOXIM 831 02T HB | LOXIM Industries Private Limited | PP Copolymer | LOXIM |
| TECACOMP® PA66 CF30 black 3519 | Ensinger GmbH | Nylon 66 | TECACOMP® |
| Pro-fax 7523 | LyondellBasell Industries | PP Impact Copolymer | Pro-fax |