LNP™ LUBRICOMP™ JX91198 compound
| Category: | PESU , Polyethersulfone |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ LUBRICOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | b1ikOl_LNP-LUBRICOMP-JX91198-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP LUBRICOMP* JX91198 is a compound based on Polyethersulfone resin containing Proprietary Filler(s). Added feature of this material is: Wear Resistant. Also known as: LNP* LUBRICOMP* Compound PDX-J-91198 Product reorder name: JX91198 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.50 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | |||
| Flow : 24 hr | 0.20 | % | ASTM D955 |
| Across Flow : 24 hr | 0.40 | % | ASTM D955 |
| Across Flow : 24 hr | 0.41 | % | ISO 294-4 |
| Flow : 24 hr | 0.17 | % | ISO 294-4 |
| Water Absorption | |||
| 24 hr, 50% RH | 0.41 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.53 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 10100 | MPa | ASTM D638 |
| -- | 9200 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Break | 117 | MPa | ASTM D638 |
| Break | 112 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Break | 1.9 | % | ASTM D638 |
| Break | 1.8 | % | ISO 527-2 |
| Flexural Modulus | |||
| -- | 8830 | MPa | ASTM D790 |
| -- | 9240 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 169 | MPa | ASTM D790 |
| -- | 161 | MPa | ISO 178 |
| Coefficient of Friction | ASTM D3702 Modified | ||
| vs. Itself - Dynamic | 0.43 | ||
| vs. Itself - Static | 0.34 | ||
| Wear Factor - Washer | 4.00 | 10^-10 in^5-min/ft-lb-hr | ASTM D3702 Modified |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 43 | J/m | ASTM D256 |
| 23°C 2 | 7.4 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 330 | J/m | ASTM D4812 |
| 23°C 3 | 27 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Energy at Peak Load | 4.20 | J | ASTM D3763 |
| -- | 2.36 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, Unannealed, 3.20 mm | 211 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 4 | 228 | °C | ISO 75-2/Af |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 to 149 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.050 | % | |
| Rear Temperature | 343 to 354 | °C | |
| Middle Temperature | 360 to 371 | °C | |
| Front Temperature | 371 to 382 | °C | |
| Processing (Melt) Temp | 354 to 371 | °C | |
| Mold Temperature | 138 to 149 | °C | |
| Back Pressure | 0.344 to 0.689 | MPa | |
| Screw Speed | 60 to 100 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Titalon® 2200ST | Titan Plastics Compounds Co., Ltd. | Nylon 66 | Titalon® |
| AKROMID® A3 GF 50 natural (2423) | AKRO-PLASTIC GmbH | Nylon 66 | AKROMID® |
| Fluon® PTFE G201 | Asahi Glass Co., Ltd. | PTFE | Fluon® |
| Hostacom G2 N02 | LyondellBasell Industries | PP Homopolymer | Hostacom |
| Pearlthane® 16N95UV | Lubrizol Advanced Materials, Inc. | TPU-Polyether | Pearlthane® |