Ultramid® B3GM35 BK30564
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | BASF Corporation |
| Trademark: | Ultramid® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | b0fw3F_Ultramid-B3GM35-BK30564.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| A glass-fibre and mineral reinforced injection moulding grade for industrial articles having medium rigidity and high dimensional stability, used e.g. for engine covers, handles, mountings, etc. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.48 | -- | g/cm³ | ISO 1183 |
| Apparent Density | 0.70 | -- | g/cm³ | |
| Melt Volume-Flow Rate (MVR) (275°C/5.0 kg) | 40.0 | -- | cm³/10min | ISO 1133 |
| Water Absorption | ISO 62 | |||
| Saturated, 23°C | 5.7 | -- | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 1.7 | -- | % | ISO 62 |
| Viscosity Number (H2SO4 (Sulphuric Acid)) | 135 | -- | cm³/g | ISO 307 |
| Mold Shrinkage - constrained 1 | 0.40 | -- | % |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Maximum operating temperature- short cycle operation | 180 | -- | °C |
| Injection | Dry | Unit | |
|---|---|---|---|
| Screw Speed | mm/sec |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 8300 | 4300 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 125 | 70.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 2.8 | 7.5 | % | ISO 527-2 |
| Tensile Creep Modulus 2(1000 hr) | 1850 | -- | MPa | ISO 899-1 |
| Flexural Stress (23°C) | 190 | 120 | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | 4.0 | -- | kJ/m² | ISO 179/1eA |
| 23°C | 6.0 | 8.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | 50 | -- | kJ/m² | ISO 179/1eU |
| 23°C | 50 | 70 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact (23°C) | 5.5 | 13 | kJ/m² | ISO 180/A |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, not annealed | 210 | -- | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 190 | -- | °C | ISO 75-2/A |
| Melting Temperature | 220 | -- | °C | ISO 11357-3 |
| CLTE - Flow (23 to 80°C) | 3.5E-5 - 4.0E-5 | -- | cm/cm/°C | ISO 11359-2 |
| Specific Heat | 1300 | -- | J/kg/°C | |
| Thermal Conductivity | 0.38 | -- | W/m/K | DIN 52612 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | 1.0E+10 | -- | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+15 | 1.0E+12 | ohms·cm | IEC 60093 |
| Relative Permittivity (1 MHz) | 3.90 | 6.20 | IEC 60250 | |
| Dissipation Factor (1 MHz) | 0.020 | 0.20 | IEC 60250 | |
| Comparative Tracking Index (Solution A) | 400 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating (1.60 mm) | HB | -- | UL 94 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.15 | % | |
| Hopper Temperature | 80.0 | °C | |
| Rear Temperature | 260 | °C | |
| Middle Temperature | 270 | °C | |
| Front Temperature | 280 | °C | |
| Nozzle Temperature | 280 | °C | |
| Processing (Melt) Temp | 270 - 290 | °C | |
| Mold Temperature | 80.0 - 90.0 | °C |
| Injection instructions |
|---|
| Residence time : <10 min |
| Note Message | |
|---|---|
| 1 . | Test box with central gating, dimensions of base (107*47*1,5) mm, processing condition: TM = 280°C, TW = 80°C |
| 2 . | strain <= 0.5%, 23°C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| PRIMALLOY® B1700 | Mitsubishi Chemical Performance Polymers, Inc. | TPE | PRIMALLOY® |
| Monprene® MP-2216 | Teknor Apex Company | TPE | Monprene® |
| AMTOPP TP15 | Inteplast Group | PP, Unspecified | AMTOPP |
| ColorRx® TPE-T84A0RXTP | LTL Color Compounders, Inc. | TPE | ColorRx® |
| LNP™ LUBRICOMP™ IFL34 compound | SABIC Innovative Plastics | Nylon 612 | LNP™ LUBRICOMP™ |