Petrotene® PP A3 G45 NTLA010 PH367
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | Petropol Industry and Trade of Polymers LTDA |
| Trademark: | Petrotene® PP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ay4vcq_Petrotene-PP-A3-G45-NTLA010-PH367.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Polypropylene homopolymer reinforced with 45% glass fiber suitable for injection molding, good set mechanical properties, aging resistance and excellent resistance to oils and greases. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Resin ID (ISO 1043) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.10 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) | 8.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.78 to 1.2 | % | ASTM D955 |
| Water Absorption (Equilibrium) | 0.030 | % | ASTM D570 |
| Ash Content | 43 to 47 | % | ASTM D2584 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 90.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 3.5 | % | ASTM D638 |
| Flexural Modulus 1(23°C) | 6200 | MPa | ASTM D790 |
| Flexural Strength | 125 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 70 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed) | 160 | °C | ASTM D648 |
| Vicat Softening Temperature | 163 | °C | ASTM D1525 2 |
| Melting Temperature | 160 | °C | ASTM D2117 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 | hr | |
| Processing (Melt) Temp | 200 to 250 | °C | |
| Mold Temperature | 40.0 to 80.0 | °C | |
| Injection Pressure | 70.0 to 120 | MPa |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | Rate B (120°C/h), Loading 1 (10 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Maxelast® N8960T | Nantong Polymax Elastomer Technology, Co., Ltd | TPE | Maxelast® |
| ACCUTECH™ CP0436G10M20CL | ACLO Compounders Inc. | PP Copolymer | ACCUTECH™ |
| Huafon HF-3795A | Huafon Group Co., Ltd. | TPU-Polyester | Huafon |
| Axiall PVC FG-9209 | Axiall Corporation | PVC, Rigid | Axiall PVC |
| LEXAN™ HFD1731 resin | SABIC Innovative Plastics Asia Pacific | PC | LEXAN™ |