MAGNUM™ 3416 SC
| Category: | ABS , ABS Resin |
| Manufacturer: | Trinseo |
| Trademark: | MAGNUM™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | axdR8o_MAGNUM-3416-SC.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
MAGNUM 3416SC is a resin with very high heat resistance and excellent processing characteristics. The mass (continuous process) ABS technology ensures an ABS resin that combines excellent processability with stable light base color that is ideal for self-coloring. Applications:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.05 | g/cm³ | ISO 1183 |
| Apparent Density | 0.65 | g/cm³ | ISO 60 |
| Melt Mass-Flow Rate (MFR) (220°C/10.0 kg) | 6.5 | g/10 min | ISO 1133 |
| Molding Shrinkage | 0.40 to 0.70 | % | ISO 294-4 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2200 | MPa | ISO 527-2 |
| Tensile Stress (Yield) | 43.0 | MPa | ISO 527-2 |
| Tensile Strain (Yield) | 3.1 | % | ISO 527-2 |
| Flexural Modulus 1 | 2200 | MPa | ISO 178 |
| Flexural Stress 2 | 76.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C | 12 | kJ/m² | |
| 23°C | 17 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | ISO 75-2/A | ||
| 1.8 MPa, Unannealed | 85.0 | °C | |
| 1.8 MPa, Annealed | 100 | °C | |
| Vicat Softening Temperature | 108 | °C | ISO 306/B50 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Burning Rate 3(2.00 mm) | 55 | mm/min | ISO 3795 |
| Flame Rating 4 | UL 94 | ||
| 1.50 mm | HB | ||
| 3.00 mm | HB | ||
| Carbon Emission | 10.0 | µg/g | VDA 277 |
| Fogging | 99 | % | ISO 6452 |
| Note Message | |
|---|---|
| 1 . | 3-points |
| 2 . | 3-points |
| 3 . | This rating not intended to reflect hazards presented by this or any other material under actual fire conditions. |
| 4 . | This rating not intended to reflect hazards presented by this or any other material under actual fire conditions. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| UNIGARD™ HP HFDA-6522 NT | The Dow Chemical Company | PE Copolymer | UNIGARD™ |
| Bergamid™ A70 G20 H BK014 | PolyOne Corporation | Nylon 66 | Bergamid™ |
| ALTECH® PA6 C 2035/507 GF35 | ALBIS PLASTIC GmbH | Nylon 6 | ALTECH® PA6 |
| APICAL 250AF029 | Kaneka Corporation | PI, TS | APICAL |
| Delene 2060 | Shanghai Lin Gen Rubber Materials Co., Ltd. | TPE | Delene |