ISPLEN® PB-110 H2E Datasheet,PP Copolymer,REPSOL-SHANGHAI SUSHENG

ISPLEN® PB-110 H2E

Category:	PP Copolymer , Polypropylene Copolymer
Manufacturer:	REPSOL
Trademark:	ISPLEN®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	awZ4ge_ISPLEN-PB-110-H2E.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

Message
ISPLEN® PB-110 H2E is a block ethylene-propylene copolymer with a high molecular weight. Due to averagely good flow properties and very high mechanical properties is a suitable grade to be processed into pipes. Its very high impact strength, even at low temperatures, and stress cracking also can use in critical conditions. Other applications are corrugated pipes for sewage, due to its high modulus ADDITIVATION ISPLEN® PB-110 H2E contains stabilizers and additives according to the end-use of the item in order to reinforce the thermal stability and increase the hot-water extraction resistance. The processor may include other additives. Formulation allows polymer stability during the normal conditions of processing and use. COLOURING ISPLEN grades are supplied in natural colour but it can be easily coloured with pigments steady at processing temperatures, using dry-colouring or masterbatch techniques. FOODSTUFF REGULATIONS ISPLEN® PB-110 H2E is approved for food contact under certain legislation. For more information about specific country regulation, please, contact with our Technical Service. ISPLEN® PB110H2E is a very low melt flow propylene heterophasic copolymer with a reinforced formulation for extrusion process, and a high thermal stabilisation. Its crystalline structure gives a high rigidity and very high tensile strength resistance. Its flow characteristics and mechanical properties make it specially adapted for high thickness and good glossy surface films or sheets. It can be easily coloured during the extrusion process using the right pigments, especially in the form of masterbatches with a higher melt flow rate than that of the base polymer. APPLICATIONS In extrusion process requiring high melt viscosity strength and particularly high tensile properties, such as: Sheets and Profiles Blow-molding Glossy surface sheets. Pipes. Recommended melt temperature range from 190 to 250°C. Processing conditions should be optimised for each production line.

Message

ISPLEN® PB-110 H2E is a block ethylene-propylene copolymer with a high molecular weight. Due to averagely good flow properties and very high mechanical properties is a suitable grade to be processed into pipes. Its very high impact strength, even at low temperatures, and stress cracking also can use in critical conditions. Other applications are corrugated pipes for sewage, due to its high modulus

ADDITIVATION
ISPLEN® PB-110 H2E contains stabilizers and additives according to the end-use of the item in order to reinforce the thermal stability and increase the hot-water extraction resistance. The processor may include other additives. Formulation allows polymer stability during the normal conditions of processing and use.

COLOURING
ISPLEN grades are supplied in natural colour but it can be easily coloured with pigments steady at processing temperatures, using dry-colouring or masterbatch techniques.

FOODSTUFF REGULATIONS
ISPLEN® PB-110 H2E is approved for food contact under certain legislation. For more information about specific country regulation, please, contact with our Technical Service.

ISPLEN® PB110H2E is a very low melt flow propylene heterophasic copolymer with a reinforced formulation for extrusion process, and a high thermal stabilisation. Its crystalline structure gives a high rigidity and very high tensile strength resistance. Its flow characteristics and mechanical properties make it specially adapted for high thickness and good glossy surface films or sheets.
It can be easily coloured during the extrusion process using the right pigments, especially in the form of masterbatches with a higher melt flow rate than that of the base polymer.

APPLICATIONS
In extrusion process requiring high melt viscosity strength and particularly high tensile properties, such as:

Sheets and Profiles

Blow-molding

Glossy surface sheets.

Pipes.

Recommended melt temperature range from 190 to 250°C. Processing conditions should be optimised for each production line.

General Information
Additive	Heat Stabilizer
Features	Block Copolymer Food Contact Acceptable Good Chemical Resistance Good Colorability Good Flow Heat Stabilized High ESCR (Stress Crack Resist.) High Molecular Weight High Rigidity High Tensile Strength Low Temperature Impact Resistance Ultra High Impact Resistance
Uses	Blow Molding Applications Corrugated Pipe Film Piping Profiles Sheet
Agency Ratings	EU Food Contact, Unspecified Rating
Appearance	Colors Available Natural Color
Forms	Pellets
Processing Method	Blow Molding Extrusion Pipe Extrusion Profile Extrusion Sheet Extrusion

Physical	Nominal Value	Unit	Test Method
Density (23°C)	0.903 to 0.905	g/cm³	ISO 1183
Melt Mass-Flow Rate (MFR)			ISO 1133
230°C/2.16 kg	0.25 to 0.30	g/10 min
230°C/5.0 kg	1.0 to 1.2	g/10 min

Hardness	Nominal Value	Unit	Test Method
Rockwell Hardness	77		ASTM D785
Shore Hardness (Shore D)	62		ISO 868

Mechanical	Nominal Value	Unit	Test Method
Tensile Stress (Yield)	28.0	MPa	ISO 527-2
Tensile Strain (Break)	> 500	%	ISO 527-2
Flexural Modulus	1200 to 1400	MPa	ISO 178

Impact	Nominal Value	Unit	Test Method
Charpy Notched Impact Strength (23°C)	55	kJ/m²	ISO 179
Notched Izod Impact Strength			ISO 180/1A
-20°C	5.0	kJ/m²
23°C	40	kJ/m²

Thermal	Nominal Value	Unit	Test Method
Heat Deflection Temperature (0.45 MPa, Unannealed)	81.0	°C	ISO 75-2/B
Vicat Softening Temperature	147	°C	ISO 306/A

Extrusion	Nominal Value	Unit
Cylinder Zone 1 Temp.	190 to 200	°C
Cylinder Zone 2 Temp.	190 to 205	°C
Cylinder Zone 3 Temp.	195 to 210	°C
Cylinder Zone 4 Temp.	195 to 215	°C
Cylinder Zone 5 Temp.	200 to 220	°C
Melt Temperature	190 to 250	°C

Resin Grade	Manufacturer	Category	Trademark
RTP 209A HI UV	RTP Company	Nylon 6	RTP
TEKNIFLEX® VPA1560	Tekni-Films, a div of Tekni-Plex	Film, PVC/PE/PCTFE	TEKNIFLEX®
ACRYLITE® Resist ZK-D	Evonik Cyro LLC	Acrylic (PMMA)	ACRYLITE®
Badamid® PA12 H UV EX	Bada AG	Nylon 12	Badamid®
Moplen HP425J	PolyMirae	PP Homopolymer	Moplen