Sipolprene® 25170
| Category: | TPC-ET , Thermoplastic Copolyester Elastomer |
| Manufacturer: | SIPOL S.p.A |
| Trademark: | Sipolprene® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | awP7U2_Sipolprene-25170.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Sipolprene® 25170 is an ether ester thermoplastic elastomer (TPC-ET), developed and manufactured by Sipol, with a nominal hardness of Shore D 27, a very low modulus, and a rheological behaviour, which makes it suitable for injection molding and extrusion processing. Sipolprene® 25170 comes in a natural color with a standard stabilisation package, fully in compliance with American FDA and European EU 10/2011 Food Contact Regulations. Black color and/or UV stabilised and/or heat stabilised are all available in dry blend version on request. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Agency Ratings |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.10 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (200°C/2.16 kg) | 12 | g/10 min | ASTM D1238, ISO 1133 |
| Water Absorption (23°C, 24 hr) | 0.76 | % | Internal Method |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 27 | ASTM D2240, ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break) | 23.0 | MPa | ASTM D638, ISO 527-2 |
| Tensile Elongation (Break) | 800 | % | ASTM D638, ISO 527-2 |
| Flexural Modulus | 30.0 | MPa | ASTM D790, ISO 178 |
| Abrasion Resistance | 42.0 | mm³ | DIN 53516 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tear Strength | 85.0 | kN/m | ASTM D1004 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | No Break | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 73.0 | °C | ISO 306/A50, ASTM D1525 1 |
| Peak Melting Temperature | 173 | °C | ASTM D3418, ISO 3146 |
| Note Message | |
|---|---|
| 1 . | Rate A (50°C/h), Loading 1 (10 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TOTAL Polyethylene HDPE MS 201 B | TOTAL Refining & Chemicals | HDPE | TOTAL Polyethylene |
| Tufel® II 94305 | Momentive Performance Materials Inc. | Silicone | Tufel® II |
| NEFTEKHIM PP 4345T | Nizhnekamskneftekhim Inc. | PP Copolymer | NEFTEKHIM PP |
| Fluoroplex F 15 - GML | UNIFLON | PTFE | Fluoroplex |
| K-Prene 7000 XL 65 | Technovinyl Polymers India Ltd. | TPV | K-Prene |