SUPREME Specialty PS SP6415
| Category: | PS (HIPS) , High Impact Polystyrene |
| Manufacturer: | Supreme Petrochem Ltd. |
| Trademark: | SUPREME Specialty PS |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | av6Ciy_SUPREME-Specialty-PS-SP6415.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
SUPREME Specialty PS SP6415 is a High Impact Polystyrene product. It can be processed by injection molding and is available in Africa & Middle East, Asia Pacific, Europe, or North America. Applications of SUPREME Specialty PS SP6415 include appliances and food contact applications. Characteristics include:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.04 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (200°C/5.0 kg) | 5.5 | g/10 min | ASTM D1238 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(23°C, 3.20 mm, Injection Molded) | 25.0 | MPa | ASTM D638 |
| Tensile Elongation 2(Break, 23°C, 3.20 mm, Injection Molded) | 30 | % | ASTM D638 |
| Flexural Modulus (23°C, 3.20 mm, Injection Molded) | 2000 | MPa | ASTM D790 |
| Flexural Strength (23°C, 3.20 mm, Injection Molded) | 45.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.20 mm, Injection Molded) | 140 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 3.20 mm, Injection Molded) | 78.0 | °C | ASTM D648 |
| Vicat Softening Temperature | 99.0 | °C | ASTM D1525 3 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.60 mm) | HB | UL 94 |
| Optical | Nominal Value | Test Method | |
|---|---|---|---|
| Gardner Gloss (60°, 3200 µm, Injection Molded) | 90 | ASTM D523 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Processing (Melt) Temp | 195 to 260 | °C | |
| Mold Temperature | 50.0 to 60.0 | °C |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | Rate B (120°C/h), Loading 1 (10 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Starflam RF0069 | Eurostar Engineering Plastics | Nylon 66 | Starflam |
| Toraycon® 1401X04 | Toray Resin Company | PBT | Toraycon® |
| HiFill FR® PA6 FR NAT | Techmer Engineered Solutions | Nylon 6 | HiFill FR® |
| Karina IVORY PVC COMPOUND -E 881-35/ 1-C-IS-AC | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Petro Rabigh PP AZ764 | Rabigh Refining & Petrochemical Co. | PP Impact Copolymer | Petro Rabigh PP |