LONOY lonoy 1200
| Category: | PC+PBT , Polycarbonate + PBT |
| Manufacturer: | Kingfa |
| Trademark: | LONOY |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | auKg0A_LONOY-lonoy-1200.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LONOY lonoy 1200 is a polycarbonate polybutene terephthalate (PC PBT) material,. This product is available in North America or Asia Pacific region. The processing method is injection molding. The main features of LONOY lonoy 1200 are:
Typical application areas include:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.23 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (260°C/5.0 kg) | 45 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (23°C) | 0.60 - 0.80 | % | ASTM D955 |
| Water Absorption (23°C, 24 hr) | 0.12 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 115 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1 | 55.0 | MPa | ASTM D638 |
| Tensile Elongation 2(Break) | 80 | % | ASTM D638 |
| Flexural Modulus 3 | 2200 | MPa | ASTM D790 |
| Flexural Strength 4 | 80.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.20 mm) | 700 | J/m | ASTM D256 |
| Unnotched Izod Impact (23°C, 3.20 mm) | No Break | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, unannealed, 6.40mm | 110 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 6.40mm | 83.0 | °C | ASTM D648 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+15 | ohms | ASTM D257 |
| Volume Resistivity | 1.0E+17 | ohms·cm | ASTM D257 |
| Dielectric Strength (1.60 mm) | 28 | kV/mm | ASTM D149 |
| Additional Information |
|---|
| Flammability, GM9070P, 1.6mm: <100 mm/min |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 110 | °C | |
| Drying Time | 3.0 - 4.0 | hr | |
| Rear Temperature | 230 - 260 | °C | |
| Middle Temperature | 240 - 270 | °C | |
| Front Temperature | 240 - 270 | °C | |
| Processing (Melt) Temp | 240 - 270 | °C | |
| Mold Temperature | 70.0 - 90.0 | °C | |
| Back Pressure | 0.300 - 0.700 | MPa |
| Injection instructions |
|---|
| Processing Temperature Limit: 280°CInjection Speed: 60 to 100% |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 2.0 mm/min |
| 4 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Fainplast PVC CKL 90/40 | Fainplast Compounds S.r.l | PVC, Unspecified | Fainplast PVC |
| Geon™ Vinyl Rigid Extrusion L6701 | PolyOne Corporation | PVC, Rigid | Geon™ Vinyl Rigid Extrusion |
| Hylon® N1240MG25L | Ravago Manufacturing Americas, LLC | Nylon 66 | Hylon® |
| Sylvin 83013-80 Black | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Sylvin 8200-70UV Black | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |