Surlyn® 9150
| Category: | EMAA , Ethylene Methacrylic Acid |
| Manufacturer: | DuPont Packaging & Industrial Polymers |
| Trademark: | Surlyn® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | atzlGx_Surlyn-9150.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Surlyn® 9150 is a zinc ionomer thermoplastic resin. It is available for use in conventional extrusion and injection equipment, to create various sheets or shapes.Surlyn® 9150 thermoplastic resin is an advanced ethylene/methacrylic acid (E/MAA) copolymer, in which the MAA acid groups have been partially neutralized with zinc ions. |
| General Information | |
|---|---|
| Features |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.970 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 4.5 | g/10 min | ASTM D1238, ISO 1133 |
| Ion Type | Zinc |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Abrasion Resistance - NBS Index | 368 | ASTM D1630 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Freezing Point | |||
| -- | 42 | °C | ISO 3146 |
| -- | 42 | °C | ASTM D3418 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 63 | ASTM D2240, ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | |||
| Yield, 23°C, Compression Molded 1 | 15.9 | MPa | ASTM D638 |
| Break, 23°C | 28.3 | MPa | ASTM D638, ISO 527-2 |
| Tensile Elongation (Break, 23°C) | 340 | % | ASTM D638, ISO 527-2 |
| Flexural Modulus (23°C) | 359 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Impact Strength | 626 | kJ/m² | ASTM D1822 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 57.0 | °C | ASTM D1525, ISO 306 |
| Peak Melting Temperature | 82.0 | °C | ASTM D3418, ISO 3146 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Haze (6350 µm) | 3.2 | % | ASTM D1003 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Processing (Melt) Temp | 185 to 285 | °C |
| Note Message | |
|---|---|
| 1 . | Type IV, 50 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SILVER® EUL60-K/SVJ/SJT-45P | Guangdong Silver Age Sci & Tech. Co., Ltd | PVC, Unspecified | SILVER® |
| Tenac™-C 3510 | Asahi Kasei Chemicals Corporation | Acetal (POM) Copolymer | Tenac™-C |
| Clearflex® FF 508 | Versalis S.p.A. | LMDPE | Clearflex® |
| HiFill® ABS GB15 | Techmer Engineered Solutions | ABS | HiFill® |
| Isocor™ HG26SI | Shakespeare Monofilaments and Specialty Polymers | Nylon 612 | Isocor™ |