Eltex® TUB 350-HM00

Category:	PP Impact Copolymer , Polypropylene Impact Copolymer
Manufacturer:	INEOS Olefins & Polymers Europe
Trademark:	Eltex®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	asePOc_Eltex-TUB-350-HM00.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

WECHAT

Message

Eltex® TUB 350-HM00 is a low melt flow rate impact copolymer specifically designed for extrusion of non pressure pipes but can also be used for other extrusion applications. It offers a very high stiffness while keeping good impact strength (even at low temperature) and excellent processability. This grade has very good long term stability and provides excellent ring stiffness in both solid and structured wall gravity pipes.

Applications

Non-pressure pipes and fittings (for drainage and sewerage, soil & waste,…)

Sheet extrusion

Blow moulding

Benefits and Features

Very high rigidity (PP-HM)

Good impact resistance

Non-filled, low density

High melt strength

Very good long term stability

Excellent processability (for solid and structured wall pipes extrusion)

General Information
Features	Good Impact Resistance Good Processability Impact Copolymer Low Flow Low Temperature Impact Resistance Ultra High Stiffness
Uses	Blow Molding Applications Fittings Piping Sheet
RoHS Compliance	Contact Manufacturer
Processing Method	Blow Molding Pipe Extrusion Sheet Extrusion

Physical	Nominal Value	Unit	Test Method
Density	0.908	g/cm³	ISO 1183
Melt Mass-Flow Rate (MFR) (230°C/2.16 kg)	0.30	g/10 min	ISO 1133

Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus ¹	1900	MPa
Tensile Stress (Yield, 4.00 mm, Injection Molded)	33.0	MPa	ISO 527-2
Tensile Strain (Yield, 4.00 mm, Injection Molded)	8.0	%	ISO 527-2
Flexural Modulus ²(23°C, 4.00 mm, Compression Molded)	1850	MPa	ISO 178

Impact	Nominal Value	Unit	Test Method
Charpy Notched Impact Strength			ISO 179/1eA
-20°C	6.0	kJ/m²
0°C	12	kJ/m²
23°C	> 50	kJ/m²

Thermal	Nominal Value	Unit	Test Method
Heat Deflection Temperature (0.45 MPa, Unannealed)	106	°C	ISO 75-2/B
Vicat Softening Temperature	158	°C	ISO 306/A
Melting Temperature	166	°C	ASTM D3417
Oxidation Induction Time (200°C)	> 50	min	EN 728

Note Message
1 .	Calculated from ring stiffness measurements carried out on 110 mm solid wall pipes.
2 .	Cooling rate = -15°C/min

Resin Grade	Manufacturer	Category	Trademark
Prime Tuff-X FR	Primex Plastics Corporation	Unspecified	Prime Tuff-X
RTP 4085 SI 2	RTP Company	PPA	RTP
VYPET VNT 835	Lavergne Group	PET	VYPET
Elastron® G G300.A75.N	Elastron USA, Inc.	SEBS	Elastron® G
EPLAMID 66 IMP NC A801	EPSAN Plastik SAN. ve TiC. A.S.	Nylon 66	EPLAMID 66