Spartech SCR7-7010F is a medium viscosity PC resin for injection molding that is approved by the FDA. It is heat stabilized and lubricated for good processing characteristics. Polycarbonate resins span a wide range of physical properties that combine to make it one of the toughest, most versatile of all engineering thermoplastics. It is well known for its exceptional impact resistance, plus it has outstanding mechanical, electrical, and optical properties. A very versatile product for a wide variety of applications, Spartech SCR7-7010F is recommended for industrial, transportation, sporting goods and electrical/electronic applications. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.20 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) | 10 | g/10 min | ASTM D1238 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (23°C) | 62.1 | MPa | ASTM D638 |
| Tensile Elongation (Break, 23°C) | 120 | % | ASTM D638 |
| Flexural Modulus (23°C) | 2340 | MPa | ASTM D790 |
| Flexural Strength (23°C) | 94.8 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 770 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed) | 137 | °C | ASTM D648 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 3.0 - 4.0 | hr | |
| Rear Temperature | 266 - 277 | °C | |
| Middle Temperature | 271 - 282 | °C | |
| Front Temperature | 282 - 299 | °C | |
| Nozzle Temperature | 277 - 304 | °C | |
| Processing (Melt) Temp | 288 - 316 | °C | |
| Mold Temperature | 71.1 - 93.3 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MARPOL® PSC 6020 | Marco Polo International, Inc. | PS (GPPS) | MARPOL® PSC |
| SABIC® LDPE 2015N0 | Saudi Basic Industries Corporation (SABIC) | LDPE | SABIC® LDPE |
| Vipel® F017-AA-00 | AOC, L.L.C. | Vinyl Ester | Vipel® |
| PENTAMID AHT H1 ungefärbt | PENTAC Polymer GmbH | Nylon 46 | PENTAMID AHT |
| Durethan® AKV 35 H2.0 SR1 901510 | LANXESS Corporation | Nylon 66 | Durethan® |