PLEXIGLAS® Satinice df23 7H, based on PLEXIGLAS® 7H, is characterized by diffuse scattering of light.

Typical properties of PLEXIGLAS® molding compound are

good flow

high mechanical strength, surface hardness and mar resistance

very good weather resistance.

Special properties of PLEXIGLAS® Satinice df23 7H are

excellent lightdiffusion combined with excellent light transmission,

matte surfaces can be obtained by varying the extrusion parameters.

Application:
Used for extruding profiles and sheets for lighting engineering applications

Examples:
luminaire covers, displays, projection screens and similar applications

General Information
Features	Good Flow Good Weather Resistance High Hardness High Strength Light Stabilized
Uses	Displays Lighting Diffusers Profiles Sheet
Forms	Pellets
Processing Method	Extrusion
Multi-Point Data	Isothermal Stress vs. Strain (ISO 11403-1) Secant Modulus vs. Strain (ISO 11403-1) Shear Modulus vs. Temperature (ISO 11403-1) Viscosity vs. Shear Rate (ISO 11403-2)

Physical	Nominal Value	Unit	Test Method
Density	1.19	g/cm³	ISO 1183
Melt Volume-Flow Rate (MVR) (230°C/3.8 kg)	0.950	cm³/10min	ISO 1133

Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus	3400	MPa	ISO 527-2/1
Tensile Stress (Break)	70.0	MPa	ISO 527-2/5
Tensile Strain (Break)	6.0	%	ISO 527-2/5

Impact	Nominal Value	Unit	Test Method
Charpy Notched Impact Strength (23°C)	1.8	kJ/m²	ISO 179/1
Charpy Unnotched Impact Strength (23°C)	20	kJ/m²	ISO 179/1eU

Thermal	Nominal Value	Unit	Test Method
Heat Deflection Temperature
0.45 MPa, Unannealed	101	°C	ISO 75-2/B
1.8 MPa, Unannealed	97.0	°C	ISO 75-2/A
Glass Transition Temperature	106	°C	ISO 11357-2
Vicat Softening Temperature	105	°C	ISO 306/B50
CLTE - Flow (0 to 50°C)	6.3E-5	cm/cm/°C	ISO 11359-2

Flammability	Nominal Value	Unit	Test Method
Glow Wire Ignition Temperature	700	°C	IEC 60695-2-13
Fire Rating	B2		DIN 4102

Additional Information	Nominal Value	Unit	Test Method
Half-Value Angle	21.0	°	DIN 5036

Optical	Nominal Value	Unit	Test Method
Transmittance ¹	81.0	%	ISO 13468-2

Extrusion	Nominal Value	Unit
Drying Temperature	< 95.0	°C
Drying Time	2.0 to 3.0	hr
Melt Temperature	220 to 260	°C
Die Temperature	220 to 260	°C

Note Message
1 .	D65

Resin Grade	Manufacturer	Category	Trademark
Sanren Q200 (1st-grade)	SINOPEC Shanghai Petrochemical Co. Ltd.	LDPE	Sanren
Complet® LCF30-PA66	PlastiComp, Inc.	Nylon 66	Complet®
Hifax X 1956 A	LyondellBasell Industries	TPO (POE)	Hifax
Karina WHITE COLOR CONCENTRATE -E 1-/105-FC-LMPA	Karina Ind. e Com. de Plásticos Ltda	PVC, Unspecified	Karina
StarMed® 9030-0000	Star Thermoplastic Alloys & Rubbers, Inc.	TPE	StarMed®