ASPIRE VINYL™ G940
| Category: | PVC, Flexible , Flexible Polyvinyl Chloride |
| Manufacturer: | Axiall Corporation |
| Trademark: | ASPIRE VINYL™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | apKvcY_ASPIREVINYLG940.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| G940 is a sustainable general purpose flexible extrusion PVC compound for interior applications. This compound contains organic-based stabilizers and bio-based plasticizers produced from renewable resources and is formulated to be phthalate-free and heavy metal-free and to meet the renewable carbon requirement for the USDA BioPreferred Program. (Testing of finished product required by customer). |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.40 - 1.44 | g/cm³ | ASTM D792 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness | ASTM D2240 | ||
| Shaw A, 10 seconds | 92 - 98 | ASTM D2240 | |
| Shaw D, 10 seconds | 46 - 52 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D638 | ||
| -- | 17.8 | MPa | ASTM D638 |
| 100% strain | 15.7 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 150 | % | ASTM D638 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | -13.4 | °C | ASTM D746 |
| Melting Temperature | 179 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Mar-Bal MB3000-15 | Mar-Bal, Inc. | Polyester, TP | Mar-Bal |
| RTP 300 AR 10 TFE 10 | RTP Company | PC | RTP |
| Megalon® 133GHSL | Mega Polymers | Nylon 66 | Megalon® |
| Karina CLEAR PVC COMPOUND -E 80/206-IS-RG | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| PLUSTEK RA304G6 | Polyram Ram-On Industries | Nylon 66 | PLUSTEK |