LUBEMID B27 NATURAL UV
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | LUBEN PLAST srl |
| Trademark: | LUBEMID |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | aogKe4_LUBEMID-B27-NATURAL-UV.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Compound based on PA6 natural first choice. Lubricated and nucleated. UV stabilized. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Appearance |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.11 to 1.15 | g/cm³ | ISO 1183/A |
| Water Absorption (23°C, 24 hr, 3.20 mm) | 2.0 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 3200 to 3800 | MPa | ISO 527-2/1A/1 |
| Tensile Stress | ISO 527-2/1A/50 | ||
| Yield | 55.0 to 75.0 | MPa | |
| Break | 40.0 to 60.0 | MPa | |
| Tensile Strain | ISO 527-2/1A/50 | ||
| Yield | 7.0 to 12 | % | |
| Break | 20 to 25 | % | |
| Flexural Modulus 1 | 2000 to 2500 | MPa | ISO 178 |
| Flexural Stress 2 | 60.0 to 80.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 4.5 to 6.5 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | No Break | ISO 179/1eU | |
| Notched Izod Impact | |||
| 23°C, 3.20 mm | 45 to 60 | J/m | ASTM D256A |
| 23°C 3 | No Break | ASTM D256 | |
| 23°C | 4.5 to 6.5 | kJ/m² | ISO 180/A |
| 23°C 4 | 4.5 to 6.0 | kJ/m² | ASTM D256 |
| Unnotched Izod Impact Strength (23°C) | No Break | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 155 to 165 | °C | ASTM D648 |
| 0.45 MPa, Unannealed | 160 to 170 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed, 3.20 mm | 55.0 to 65.0 | °C | ASTM D648 |
| Vicat Softening Temperature | |||
| -- | 205 to 215 | °C | ISO 306/A120 |
| -- | 200 to 210 | °C | ISO 306/B120 |
| Melting Temperature | 210 to 225 | °C | Internal Method |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Glow Wire Flammability Index (2.00 mm) | 750 | °C | IEC 60695-2-12 |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| 3 . | Notch E |
| 4 . | Notch A |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SABIC® Vestolen A 6060R 65307 | Saudi Basic Industries Corporation (SABIC) | HDPE | SABIC® Vestolen A |
| Sindustris PP R7701 | Sincerity Australia Pty Ltd. | PP, Unspecified | Sindustris PP |
| CALP 1440G | Lion Idemitsu Composites Co., Ltd. | Polyolefin, Unspecified | CALP |
| Glasrod HIR | Glastic Corporation | Polyester, TS | Glasrod |
| MACOMASS PP MM-PP HI 53 | MACOMASS Verkaufs AG | PP Homopolymer | MACOMASS PP |