Order Products : sales@su-jiao.com
INEOS PP L12Z-00
| Category: | PP Impact Copolymer , Polypropylene Impact Copolymer |
| Manufacturer: | INEOS Olefins & Polymers USA |
| Trademark: | INEOS PP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | aoS6NC_INEOS-PP-L12Z-00.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| L12Z-00 is a medium melt flow rate, high-stiffness, high-impact polypropylene copolymer for use in consumer products, housewares, office furniture, toys and juvenile products. It offers excellent stiffness and impact, fast cycle time, and low statics. This material has been recognized by UL for sustained use at 65°C and meets the requirements of the U.S. Food and Drug Administration as specified in 21 CFR 177.1520. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.903 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 12 | g/10 min | ASTM D1238 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 91 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1 | ASTM D638 | ||
| Yield | 28.1 | MPa | |
| Break | 18.7 | MPa | |
| Tensile Elongation 2 | ASTM D638 | ||
| Yield | 5.4 | % | |
| Break | 110 | % | |
| Flexural Modulus - 1% Secant | 1470 | MPa | ASTM D790A |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| -20°C | 47 | J/m | |
| 23°C | 140 | J/m | |
| Notched Izod Impact (Area) | ASTM D256 | ||
| -20°C | 4.62 | kJ/m² | |
| 23°C | 13.8 | kJ/m² | |
| Instrumented Impact, Ductility | ASTM D3763 | ||
| -20°C | Mixed | ||
| 23°C | Ductile |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 111 | °C | |
| 1.8 MPa, Unannealed | 56.7 | °C | |
| Vicat Softening Temperature | 151 | °C | ASTM D1525 |
| RTI Elec (1.50 mm) | 65.0 | °C | UL 746 |
| RTI Imp (1.50 mm) | 65.0 | °C | UL 746 |
| RTI Str (1.50 mm) | 65.0 | °C | UL 746 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.50 mm) | HB | UL 94 |
| Optical | Nominal Value | Test Method | |
|---|---|---|---|
| Gloss (60°) | 75 | ASTM D2457 |
| Note Message | |
|---|---|
| 1 . | 51 mm/min |
| 2 . | 51 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| CERTENE™ LLHF-120C | Muehlstein | LLDPE | CERTENE™ |
| Dow ENDURANCE™ HFDB-0801 BK EC | The Dow Chemical Company | PE Copolymer | Dow ENDURANCE™ |
| Karina CLEAR PVC COMPOUND -E 57/200-D-AT-IS-SI-SD | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| LNP™ THERMOCOMP™ EC004XXC compound | SABIC Innovative Plastics | PEI | LNP™ THERMOCOMP™ |
| Sylvin 9782-77 Black | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |