InnoTooling™ IE-644-04
| Category: | TSU , Polyurethane Thermoset Elastomer |
| Manufacturer: | Innovative Polymers, Inc. |
| Trademark: | InnoTooling™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | an1dZT_InnoTooling-IE-644-04.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| IE-644-04 is a tough, abrasion resistant elastomer formulated for room temperature hand-batch processing. Excellent physical properties can be obtained with a room temperature cure without the utilization of mercury, MOCA, or TDI. IE-644-04 is ideal for very large parts as well as mass casting. |
| General Information | |
|---|---|
| Features |
|
| RoHS Compliance |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | |
|---|---|---|---|
| Specific Gravity | |||
| Cured | 1.14 | g/cm³ | |
| Base Resin | 1.14 | g/cm³ | |
| Hardener | 1.18 | g/cm³ |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flexural Modulus | 262 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 320 | J/m | ASTM D256 |
| Thermoset | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Thermoset Components | |||
| Hardener | Mix Ratio by Volume: 48 Mix Ratio by Weight: 50 | ||
| Resin | Mix Ratio by Weight: 100 Mix Ratio by Volume: 100 | ||
| Demold Time | 240 to 480 | min |
| Uncured Properties | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Viscosity | |||
| 25°C 1 | 0.080 | Pa·s | |
| 25°C 2 | 2.8 | Pa·s | |
| 25°C 3 | 5.8 | Pa·s | |
| Curing Time 4 | 40 | hr | |
| Gel Time | 20 to 30 | min |
| Cured Properties | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D) | 50 to 60 | ASTM D2240 | |
| Tensile Strength | 19.3 | MPa | ASTM D638 |
| Tensile Elongation at Break | 20 | % | ASTM D638 |
| Tear Strength | 61.3 | kN/m | ASTM D624 |
| Note Message | |
|---|---|
| 1 . | Hardener |
| 2 . | Mixed |
| 3 . | Resin |
| 4 . | 24 hours at 77°F + 16 hours at 150°F |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Quadrant EPP ERTALON® 6 PLA | Quadrant Engineering Plastic Products | Nylon 6 | Quadrant EPP |
| Quadrant EPP ERTACETAL® C/3WF | Quadrant Engineering Plastic Products | Acetal (POM) Copolymer | Quadrant EPP |
| 4LAC® 10H20800 | 4Plas | ABS | 4LAC® |
| LEXAN™ HFD1930 resin | SABIC Innovative Plastics | PC | LEXAN™ |
| Petroquim PP PH 0322 | Petroquim S.A. | PP Homopolymer | Petroquim PP |