Rilsamid® AESN Noir P212 CTL
| Category: | Nylon 12 , Polyamide 12 |
| Manufacturer: | Arkema |
| Trademark: | Rilsamid® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | amxqwe_Rilsamid-AESN-Noir-P212-CTL.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Rilsamid® AESN Noir P212 CTL is a plasticized conductive grade designed for tube extrusion. AESN Noir P212 CTL is specially designed for conductive multi-layers fuel line applications. MAIN APPLICATIONS
|
| General Information | |
|---|---|
| Additive |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.14 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (235°C/5.0 kg) | 1.60 | cm³/10min | ISO 11357 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness | ISO 868 | ||
| Shore D | 75 | ||
| Shore D, 15 sec | 69 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 860 | MPa | ISO 527-2 |
| Tensile Stress | ISO 527-2 | ||
| Yield | 32.0 | MPa | |
| Break | 38.0 | MPa | |
| Tensile Strain | ISO 527-2 | ||
| Yield | 23 | % | |
| Break | > 200 | % | |
| Flexural Modulus | 820 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | ||
| -30°C | 6.0 | kJ/m² | |
| 23°C | 48 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179 | ||
| -30°C | No Break | ||
| 23°C | No Break |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melting Temperature | 174 | °C | ISO 11357-3 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | < 1.0E+4 | ohms | ISO 3915 |
| Additional Information | Nominal Value | Test Method | |
|---|---|---|---|
| ISO Shortname | PA12, EHLZ, 22-010 | ISO 1874 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 4.0 to 6.0 | hr | |
| Melt Temperature | 230 to 270 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| NILFLEX® SH A90 MC009 | Taro Plast S.p.A. | SEBS | NILFLEX® |
| CYCOM® 7701 | Cytec Industries Inc. | Epoxy | CYCOM® |
| Elastollan® L 765 D | BASF Polyurethanes GmbH | TPU-Polyester | Elastollan® |
| ELASTOSIL® N 189 | Wacker Chemie AG | Silicone | ELASTOSIL® N |
| P-FLEX 020 | Putsch Kunststoffe GmbH | ABS | P-FLEX |