CERTENE™ LDF-0822A
| Category: | LDPE , Low Density Polyethylene |
| Manufacturer: | Muehlstein |
| Trademark: | CERTENE™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | amZ92U_CERTENE-LDF-0822A.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| LDF-0822A is a certified prime resin specially designed for production of shrink wrapping Blown films for case bundling applications requiring excellent shrink performance, very high toughness, good puncture and burn-through resistance. LDF-0822A is also recommended for impact liner films. It features easy processability with excellent film optical and mechanical properties. Minimum recommended film thickness is 1.5 mils. LDF-0822A contains no slip and no antiblock. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.922 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.80 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 38 | µm | |
| secant modulus | ASTM D882 | ||
| 1% secant, MD : 38 µm | 186 | MPa | ASTM D882 |
| 1% secant, TD : 38 µm | 235 | MPa | ASTM D882 |
| Tensile Strength | ASTM D882 | ||
| MD : Yield, 38 µm | 12.0 | MPa | ASTM D882 |
| TD : Yield, 38 µm | 12.0 | MPa | ASTM D882 |
| MD : Fracture, 38 µm | 31.0 | MPa | ASTM D882 |
| TD : Fracture, 38 µm | 23.0 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Fracture, 38 µm | 220 | % | ASTM D882 |
| TD : Fracture, 38 µm | 550 | % | ASTM D882 |
| Dart Drop Impact (38 µm) | 95 | g | ASTM D1709A |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 38 µm | 720 | g | ASTM D1922 |
| TD : 38 µm | 140 | g | ASTM D1922 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°, 38.1 µm) | 60 | ASTM D2457 | |
| Haze (38.1 µm) | 6.8 | % | ASTM D1003 |
| Additional Information |
|---|
| This Specimen was compression molded and was tested according to ASTM D1928 Procedure C. |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 180 - 210 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Evermore PUR SW-8021HR | Evermore Chemical Industry Co., Ltd. | PUR, Unspecified | Evermore PUR |
| HiFill® PPA GF35 IM AHWR | Techmer Engineered Solutions | PPA | HiFill® |
| PENTAMID A GV30 H yellow 1023/1 | PENTAC Polymer GmbH | Nylon 66 | PENTAMID A |
| Osterlene® LD02520A | Osterman & Company | LDPE | Osterlene® |
| Styropek® BF 495 | Styropek S.A. de C.V. | PS (EPS) | Styropek® |