INEOS Wire & Cable BP28D780 Datasheet,LDPE,INEOS Olefins & Polymers Europe-SHANGHAI SUSHENG

Message
BP28D780 is a low density polyethylene compound suitable for the thin walled insulation of telephone wires. BP28D780 combines good processability at very high extrusion speeds with excellent mechanical properties, a high resistance to copper catalysed thermal oxidation and excellent resistance to petroleum jelly absorption. The combination of these properties in BP28D780 makes it suitable for use as telephone singles insulation in air spaced and filled cables and in environments subject to high temperatures. BP 28 D780 contains a metal deactivator.

General Information
Additive	Metal deactivator
Features	Workability, good
Uses	Wire and cable applications Communication wire insulation material
Agency Ratings	ASTM D 1248, II, Class A, Cat. 5, Grade D5 ASTM D 1248, II, Class A, Cat. 5, Grade E4 BS 3573 BS 6234 Type 03 BT M 237B CENELEC HD 624.3 S1, L/MD Solid CNET CM 24 IEC 60708 ISO 1872 PE KHKN 27D003 VDE 0207, Part 103, L/MD Solid VDE 0207, Part 2, Type 2Y12
RoHS Compliance	Contact manufacturer
Forms	Particle

Physical	Nominal Value	Unit	Test Method
Density	0.929	g/cm³	ISO 1183/D
Melt Mass-Flow Rate (MFR) (190°C/2.16 kg)	0.25	g/10 min	ISO 1133

Hardness	Nominal Value	Unit	Test Method
Durometer Hardness (Shore D, 1 sec)	56		ISO 868

Mechanical	Nominal Value	Unit	Test Method
Tensile Stress			IEC 60811-1-1
Yield	15.0	MPa	IEC 60811-1-1
Fracture	18.0	MPa	IEC 60811-1-1
Tensile Strain (Break)	550	%	IEC 60811-1-1

Thermal	Nominal Value	Unit	Test Method
Vicat Softening Temperature	106	°C	ISO 306/A

Electrical	Nominal Value		Test Method
Dielectric Constant (1 MHz)	2.28		ASTM D1531
Dissipation Factor (1 MHz)	1.0E-4		ASTM D1531

Additional Information
Properties of Insulation with 0.2 mm radial thickness on 0.5 mm diameter copper conductors:-Tensile Strength at Break, IEC 811-1-1: 20 MPa-Elongation, IEC 811-1-1: 600%-Ageing in Air, Retention of Tensile Properties, IEC 811-1-2, 10 days, 100°C: 90%-Petroleum Jelly Absorption Weight Gain, IEC 811-4-2, Preconditioned in Petroleum Jelly, 10 days, 70°C: 11%-Retention of Tensile Properties, IEC 811-1-1, Preconditioned in Petroleum Jelly, 10 days, 70°C: 90%-Resistance to Ageing in Air at 105°C, BT M237, IEC 811-4-2, Preconditioned in Petroleum Jelly, 14 days, 60°C: 1500 h

Additional Information

Properties of Insulation with 0.2 mm radial thickness on 0.5 mm diameter copper conductors:-Tensile Strength at Break, IEC 811-1-1: 20 MPa-Elongation, IEC 811-1-1: 600%-Ageing in Air, Retention of Tensile Properties, IEC 811-1-2, 10 days, 100°C: 90%-Petroleum Jelly Absorption Weight Gain, IEC 811-4-2, Preconditioned in Petroleum Jelly, 10 days, 70°C: 11%-Retention of Tensile Properties, IEC 811-1-1, Preconditioned in Petroleum Jelly, 10 days, 70°C: 90%-Resistance to Ageing in Air at 105°C, BT M237, IEC 811-4-2, Preconditioned in Petroleum Jelly, 14 days, 60°C: 1500 h

Extrusion	Nominal Value	Unit
Melt Temperature	210 - 280	°C

Extrusion instructions
Screw L/D ratio: >20:1Compression ratio: >3

Resin Grade	Manufacturer	Category	Trademark
TAROMID A 280 G2 Y0	Taro Plast S.p.A.	Nylon 66	TAROMID A
TOTAL Polystyrene Impact 4241	TOTAL Refining & Chemicals	PS (HIPS)	TOTAL Polystyrene
Celstran® PP-GF30-0455 P10/10	Celanese Corporation	PP, Unspecified	Celstran®
Geon™ Vinyl Flexible 90043	PolyOne Corporation	PVC, Flexible	Geon™ Vinyl Flexible
Hanwha Total PP TB92R	HANWHA TOTAL PETROCHEMICALS Co., Ltd.	PP, High Crystal	Hanwha Total PP

Category:	LDPE , Low Density Polyethylene
Manufacturer:	INEOS Olefins & Polymers Europe
Trademark:	INEOS Wire & Cable
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	amVq3G_INEOS-Wire-Cable-BP28D780.pdf
PRICE:	Order Products email sales@su-jiao.com