Hytrel® G3548 NC010
| Category: | TPC-ET , THERMOPLASTIC POLYESTER ELASTOMER |
| Manufacturer: | DuPont Performance Polymers |
| Trademark: | Hytrel® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | amQHIU_Hytrel-G3548-NC010.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 35 Shore D Standard Performance Polyester Elastomer with Non-discoloring Stabilizer |
| General Information | |
|---|---|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Multi-Point Data |
|
| Part Marking Code (ISO 11469) |
|
| Resin ID (ISO 1043) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.15 | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | ||
| Across Flow | 0.90 | % | |
| Flow | 0.70 | % | |
| Water Absorption | |||
| 24 hr | 6.9 | % | ASTM D570 |
| 23°C, 24 hr, 2.00 mm | 12 | % | ISO 62 |
| Equilibrium, 23°C, 2.00 mm, 50% RH | 0.80 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D, 15 sec) | 24 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 25.0 | MPa | ISO 527-2 |
| Tensile Stress | ISO 527-2 | ||
| Break | 10.0 | MPa | |
| 5.0% Strain | 1.50 | MPa | |
| 10% Strain | 2.50 | MPa | |
| 50% Strain | 6.00 | MPa | |
| Tensile Strain (Break) | 190 | % | ISO 527-2 |
| Nominal Tensile Strain at Break | 200 | % | ISO 527-2 |
| Flexural Modulus | 25.0 | MPa | ISO 178 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tear Strength | ISO 34-1 | ||
| Across Flow | 80 | kN/m | |
| Flow | 60 | kN/m |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -40°C | No Break | ||
| -30°C | No Break | ||
| 23°C | No Break |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melting Temperature 1 | 157 | °C | ISO 11357-3 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flammability Classification (1.50 mm) | HB | IEC 60695-11-10, -20 |
| Note Message | |
|---|---|
| 1 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| ChronoFlex® C 80A | CardioTech International, Inc. | PUR, Unspecified | ChronoFlex® |
| Karina SANDALWOOD PVC COMP. -E 856-08/471-Y-ERYB | Karina Ind. e Com. de Plásticos Ltda | PVC, Rigid | Karina |
| LG PMMA BA525 | LG MMA Corp. | Acrylic (PMMA) | LG PMMA |
| LNP™ THERMOCOMP™ WF008 compound | SABIC Innovative Plastics | PBT | LNP™ THERMOCOMP™ |
| 3M™ Dyneon™ PTFE Compound TF 6103N | 3M Advanced Materials Division | PTFE | 3M™ Dyneon™ PTFE Compound |