Petrothene® M2512
| Category: | LDPE , Low Density Polyethylene |
| Manufacturer: | LyondellBasell Industries |
| Trademark: | Petrothene® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | akh9gM_Petrothene-M2512.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PETROTHENE M 2512 is a film grade resin that exhibits good optics, good impact strength and good tensile properties and stiffness. This resin is typically used for general-purpose packaging. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.925 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 1.2 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 25 | µm | |
| Secant Modulus | ASTM D882 | ||
| 1% Secant, MD : 25 µm | 221 | MPa | |
| 1% Secant, TD : 25 µm | 262 | MPa | |
| Tensile Strength | ASTM D882 | ||
| MD : Break, 25 µm | 23.1 | MPa | |
| TD : Break, 25 µm | 19.3 | MPa | |
| Tensile Elongation | ASTM D882 | ||
| MD : Break, 25 µm | 330 | % | |
| TD : Break, 25 µm | 500 | % | |
| Dart Drop Impact (25 µm) | 85 | g | ASTM D1709 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (60°, 25.4 µm) | 100 | ASTM D2457 | |
| Haze (25.4 µm) | 7.5 | % | ASTM D1003 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 182 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| ULTEM™ HU2110 resin | SABIC Innovative Plastics | PEI | ULTEM™ |
| NORYL™ BN9003G resin | SABIC Innovative Plastics | PPE+PS | NORYL™ |
| ALCUDIA® LDPE PE-063/A | REPSOL | LDPE | ALCUDIA® LDPE |
| Kuraray Poval® PVA 220 | Kuraray Co., Ltd. | PVOH | Kuraray Poval® |
| EPAMOULD 685A26 | Epaflex Polyurethanes S.R.L. | TPU-Polyester | EPAMOULD |