ISOTHANE® 1680A-EL
| Category: | TPU-Polyether , Thermoplastic Polyurethane Elastomer (Polyether) |
| Manufacturer: | Great Eastern Resins Industrial Co Ltd (GRECO) |
| Trademark: | ISOTHANE® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | afnEbg_ISOTHANE-1680A-EL.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| ISOTHANE 1680A-EL products is polyether based thermoplastic polyurethanes with good balanced qualities. It exhibits high moisture vapor transmission. The product can be injected, extruded and blowed. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Hardness | Nominal Value | Test Method | |
|---|---|---|---|
| Durometer Hardness (Shore A) | 80 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Ross Flex 1(-6°C) | No Break | ASTM D1052 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Water Vapor Transmission 2 | 10000 | g/m²/24 hr | ASTM E96 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (300% Strain) | 7.50 | MPa | ASTM D412 |
| Tensile Strength (Yield) | 18.0 | MPa | ASTM D412 |
| Tensile Elongation (Break) | 850 | % | ASTM D412 |
| Tear Strength 3 | 7.80 | kN/m | ASTM D624 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Peak Melting Temperature | 120 | °C | ASTM D3418 |
| Note Message | |
|---|---|
| 1 . | 150000 times |
| 2 . | Procedure BW |
| 3 . | Die C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 803 TFE 20 | RTP Company | Acetal (POM) Copolymer | RTP |
| Chemlon® A30 | Teknor Apex Company (Chem Polymer) | Nylon 66 | Chemlon® |
| Daelim Po1y® PP-241W | DAELIM INDUSTRIAL CO., LTD. | PP Impact Copolymer | Daelim Po1y® |
| Ferro PP TPP30AN60GY | Ferro Corporation | PP, Unspecified | Ferro PP |
| OTECH TPO OTO9097 - Cord Insulation | OTECH Corporation | TPO | OTECH TPO |