Tarnamid® T- 27 MTR
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Grupa Azoty S.A. |
| Trademark: | Tarnamid® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | aecX2S_Tarnamid-T--27-MTR.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Tarnamid T-27 MTR there is translucent polyamide 6, with limited translucency up to maximum 2,5 mm of parts wall thickness. |
| General Information | |
|---|---|
| Uses |
|
| Appearance |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.13 | -- | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (275°C/5.0 kg) | 110 | -- | cm³/10min | ISO 1133 |
| Molding Shrinkage | ISO 294-4 | |||
| Across Flow : 2.00 mm | 0.30 | -- | % | |
| Flow : 2.00 mm | 0.15 | -- | % | |
| Water Absorption | ISO 62 | |||
| Saturation, 23°C | 9.5 | -- | % | |
| Equilibrium, 23°C, 50% RH | 2.0 | -- | % |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Ball Indentation Hardness (H 358/30) | 80.0 | 45.0 | MPa | ISO 2039-1 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 2600 | 1300 | MPa | ISO 527-2/1 |
| Tensile Stress (Yield) | 80.0 | 45.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Break) | 50 | > 100 | % | ISO 527-2/50 |
| Flexural Modulus 1 | 2200 | 1000 | MPa | ISO 178 |
| Flexural Stress 2 | 85.0 | 30.0 | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Unnotched Impact Strength (-30°C) | 5.5 | 13 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact Strength | 120 | 75 | kJ/m² | ISO 180 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 50.0 | -- | °C | ISO 75-2/A |
| Vicat Softening Temperature | 120 | -- | °C | ISO 306/B |
| Melting Temperature | 221 | -- | °C | ISO 11357-3 |
| Limit of Temperature - a few hours operation | < 180 | -- | °C | |
| Temperature Index | ||||
| 20000 hr | 70 | -- | °C | |
| 5000 hr | 85 | -- | °C |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Burning Rate | + | -- | FMVSS 302 |
| Additional Information | Dry | Conditioned | Test Method | |
|---|---|---|---|---|
| ISO Type | PA6, MT, 14-030 | -- | ISO 1874 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | 1.0E+16 | 1.0E+14 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+16 | 1.0E+13 | ohms·cm | IEC 60093 |
| Electric Strength (2.00 mm) | 30 | 24 | kV/mm | IEC 60243-1 |
| Dielectric Constant (1 Hz) | 3.50 | 4.20 | IEC 60250 | |
| Dissipation Factor (1 Hz) | 0.018 | 0.10 | IEC 60250 | |
| Comparative Tracking Index (Solution A) | 600 | 600 | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating | UL 94 | |||
| 1.60 mm | V-2 | -- | ||
| 3.20 mm | V-2 | -- | ||
| Glow Wire Flammability Index (2.00 mm) | 750 | -- | °C | IEC 60695-2-12 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | < 80.0 | °C | |
| Suggested Max Moisture | < 0.10 | % | |
| Suggested Max Regrind | 50 | % | |
| Processing (Melt) Temp | 240 to 260 | °C | |
| Mold Temperature | 40.0 to 60.0 | °C | |
| Injection Pressure | 80.0 to 110 | MPa | |
| Injection Rate | Fast |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| PRIMALENE WPP513ED05 | Southern Polymer, Inc. | EVA | PRIMALENE |
| Prime Polypro™ J708UG | Prime Polymer Co., Ltd. | PP Copolymer | Prime Polypro™ |
| Tecotek® PC44 GR10 GR003 ZG70 | Eurotec Engineering Plastics | PC | Tecotek® |
| Viprene™ P50A-22U-NAT | Alliance Polymers & Services | TPV | Viprene™ |
| ESTYRENICS 153D | PCC Plastics & Consultations Center | PS (GPPS) | ESTYRENICS |