Order Products : sales@su-jiao.com
Trademark PE LLH2942
| Category: | LLDPE , Linear Low Density Polyethylene |
| Manufacturer: | Trademark Plastics Corporation |
| Trademark: | Trademark PE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | adtA8g_Trademark-PE-LLH2942.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Trademark PE LLH2942 is a linear low density polyethylene product,. It can be processed by blown film or cast film and is available in North America. The application fields of Trademark PE LLH2942 include film, agriculture, cleaning application and food contact application. Features include:
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.942 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 2.0 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 25 | µm | |
| secant modulus | ASTM D882 | ||
| 1% secant, MD : 25 µm, blown film | 545 | MPa | ASTM D882 |
| 1% secant, TD : 25 µm, blown film | 689 | MPa | ASTM D882 |
| Tensile Strength | ASTM D882 | ||
| MD : Broken, 25 µm, blown film | 49.0 | MPa | ASTM D882 |
| TD : Broken, 25 µm, blown film | 41.4 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Broken, 25 µm, blown film | 760 | % | ASTM D882 |
| TD : Broken, 25 µm, blown film | 920 | % | ASTM D882 |
| Dart Drop Impact (25 µm, Blown Film) | < 50 | g | ASTM D1709 |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 25 µm, blown film | 20 | g | ASTM D1922 |
| TD : 25 µm, blown film | 110 | g | ASTM D1922 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°, 25.4 µm, Blown Film) | 41 | ASTM D2457 | |
| Haze (25.4 µm, Blown Film) | 18 | % | ASTM D1003 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 177 - 204 | °C |
| Extrusion instructions |
|---|
| Blow-up ratio: 2:1 or higher |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Precision Polymer N70W | Precision Polymer Engineering Ltd. | NBR | Precision Polymer |
| SCHULAMID® 66/6 MT 20 K1849 | A. Schulman Europe | Nylon 66/6 | SCHULAMID® |
| UBESTA XPA 9055 X1 | UBE Engineering Plastics, S.A. | Nylon 12 Elast | UBESTA |
| Kumho ASA XC180G | Korea Kumho Petrochemical Co., Ltd. | ASA | Kumho ASA |
| ESTOPLAST EP 2030NN21 | Ester Industries Ltd. | PBT | ESTOPLAST EP |