UNIVAL™ DMDC-6143 NT 7
| Category: | HDPE , High Density Polyethylene Resin |
| Manufacturer: | The Dow Chemical Company |
| Trademark: | UNIVAL™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | aboq4o_UNIVAL-DMDC-6143-NT-7.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
UNIVAL™ DMDC-6143 NT 7 High Density Polyethylene (HDPE) Resin is a polymer with broad molecular weight distribution and high molecular weight polymer. This product provides good stability, which contributes to uniform wall thickness in large parts, making it ideal for blow molding of containers, such as the 5-30 gallon (19-114 liter) tight-head pails, and other large parts. The broad molecular weight distribution of this resin contributes to the outstanding environmental stress crack resistance (ESCR), good rigidity level and extrudability it offers. |
| General Information | |
|---|---|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.952 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/21.6 kg) | 14 | g/10 min | ASTM D1238 |
| Environmental Stress-Cracking Resistance (50°C, 100% Igepal, F50) | 1100 | hr | ASTM D1693 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 65 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D638 | ||
| Yield | 23.4 | MPa | ASTM D638 |
| Fracture | 37.9 | MPa | ASTM D638 |
| Tensile Elongation | ASTM D638 | ||
| Yield | 10 | % | ASTM D638 |
| Fracture | 900 | % | ASTM D638 |
| Flexural Modulus - 2% Secant | 1020 | MPa | ASTM D790B |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Impact Strength 1 | 357 | kJ/m² | ASTM D1822 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed) | 67.0 | °C | ASTM D648 |
| Brittleness Temperature | < -76.1 | °C | ASTM D746 |
| Vicat Softening Temperature | 129 | °C | ASTM D1525 |
| Melting Temperature (DSC) | 131 | °C | Internal method |
| Peak Crystallization Temperature (DSC) | 125 | °C | Internal method |
| Additional Information |
|---|
| 根据 ASTM D 4976 进行基板模制和测试。 |
| Note Message | |
|---|---|
| 1 . | Type s |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Ravago Compounds HMP-305 (Roto) | Ravago Manufacturing Americas, LLC | MDPE | Ravago Compounds |
| Network Polymers HDPE 50 0355 | Network Polymers, Inc. | HDPE | Network Polymers HDPE |
| ASTALOY™ PC/ABS KMX | Marplex Australia Pty. Ltd. | PC+ABS | ASTALOY™ |
| LubriOne™ AT-000/05T 2S | PolyOne Corporation | Acetal (POM) Copolymer | LubriOne™ |
| PELPRENE™ S3002 | TOYOBO America, Inc. | TPEE | PELPRENE™ |