LIHAN® A9705P
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Nanjing Lihan Chemical Co., Ltd. |
| Trademark: | LIHAN® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | abcYbi_LIHAN-A9705P.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| LIHAN® A9705P is a Polyamide 66 (Nylon 66) product. It can be processed by injection molding and is available in Asia Pacific. Primary characteristic: flame rated. |
| General Information | |
|---|---|
| Forms |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.35 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | 0.20 to 0.40 | -- | % | |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 0.40 to 0.80 | -- | % | ISO 62 |
| Water Content | 5.5 to 6.5 | -- | % | ISO 62 |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Rockwell Hardness (R-Scale) | 120 | 115 | ISO 2039-2 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Stress (Break) | 145 | -- | MPa | ISO 527-2 |
| Tensile Strain (Break) | 1.5 | 3.0 | % | ISO 527-2 |
| Flexural Modulus | 7000 | 5000 | MPa | ISO 178 |
| Flexural Stress | 200 | -- | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Notched Izod Impact Strength | 6.5 | 10 | kJ/m² | ISO 180 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 255 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 250 | -- | °C | ISO 75-2/A |
| Melting Temperature | 260 | -- | °C | DSC |
| CLTE - Flow | 2.5E-5 to 3.5E-5 | 6.0E-5 to 8.0E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | 1.0E+13 | 1.0E+10 | ohms | ASTM D257 |
| Dielectric Strength | 17 | -- | kV/mm | ASTM D149 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating (1.59 mm) | V-0 | -- | UL 94 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Processing (Melt) Temp | 260 to 280 | °C | |
| Mold Temperature | 60.0 to 80.0 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| THERMOLAST® A TA7AOZ (Series: UV/AD1) | KRAIBURG TPE | TPE | THERMOLAST® A |
| Elastollan® 1195A50 | BASF Corp. Thermoplastic Polyurethanes | TPU-Polyether | Elastollan® |
| Hifax CA 1110 G2 | LyondellBasell Industries | PP Impact Copolymer | Hifax |
| MAJORIS FTR212 - 8229 | AD majoris | PP, Unspecified | MAJORIS |
| Infino GW-1029 | LOTTE ADVANCED MATERIALS CO., LTD. | PC | Infino |