Vyncolit X620/1 is a glass fiber and graphite filled phenolic molding compound with excellent tribological properties and excellent chemical resistance in several media.

General Information
Filler / Reinforcement	Glass \graphite
Appearance	Black
Forms	Particle
Processing Method	Resin transfer molding Compression molding Injection molding

Physical	Nominal Value	Unit	Test Method
Density	1.67	g/cm³	ISO 1183
Apparent Density	0.74	g/cm³	ISO 60
Molding Shrinkage - Flow	0.20	%	ISO 294-4
Water Absorption (23°C, 24 hr)	0.050	%	ISO 62
Post Shrinkage	0.020	%	ISO 2577

Mechanical	Nominal Value	Unit	Test Method
Flexural Strain at Break	0.90	%	ISO 178
Tensile Modulus (Injection Molded)	18000	MPa	ISO 527-2
Tensile Stress (Break, Injection Molded)	67.0	MPa	ISO 527-2
Tensile Strain (Break, Injection Molded)	0.49	%	ISO 527-2
Flexural Modulus (Injection Molded)	16000	MPa	ISO 178
Flexural Stress (Injection Molded)	133	MPa	ISO 178
Compressive Stress	171	MPa	ISO 604

Impact	Nominal Value	Unit	Test Method
Charpy Notched Impact Strength (Injection Molded)	2.7	kJ/m²	ISO 179
Charpy Unnotched Impact Strength	6.9	kJ/m²	ISO 179

Thermal	Nominal Value	Unit	Test Method
Heat Deflection Temperature (1.8 MPa, Unannealed)	> 250	°C	ISO 75-2/A
Linear thermal expansion coefficient			ASTM E831
Flow	1.1E-5	cm/cm/°C	ASTM E831
Lateral	3.9E-5	cm/cm/°C	ASTM E831

Injection	Nominal Value	Unit
Rear Temperature	60.0	°C
Middle Temperature	73.9	°C
Nozzle Temperature	87.8	°C
Processing (Melt) Temp	98.9 - 116	°C
Mold Temperature	166 - 188	°C
Injection Pressure	100 - 248	MPa
Holding Pressure	30.0 - 89.6	MPa
Back Pressure	4.83 - 15.2	MPa

Injection instructions
Plastication: 50rpmInjection Time: 2 to 8 secHold Time: 1 to 5 sec/mmCure Time, 0.125 in: 5 to 12 sec/mmAll ISO properties listed were tested in accordance with ISO 3167The value listed as Molding Shrinkage, ISO 294-4, was tested in accordance with ISO 2577.ISO Type: PF 2 C1Powder Density, ISO 60: 0.65 to 0.8 g/cm³Post Shrinkage, ISO 2577: 0.01 to 0.08%HDT A (1.80 MPa) Unannealed, ISO 75A, Injection Molding: 200 to 220°CHDT A (8.0 MPa) Unannealed, ISO 75A, Injection Molding: 175 to 195°CCLTE, Flow (TMA), ASTM E831, Injection Molding: 15 to 25 cm^-6/cm°CCLTE, Transverse (TMA), ASTM E831, Injection Molding: 30 to 40 cm^-6/cm°CFlexural Strength, ISO 178, Injection Molding: 120 to 140 MPaFlexural Modulus, ISO 178, Injection Molding: 13.5 to 15.5 GPaStrain to failure in Flexure, ISO 178, Injection Molding: 0.85 to 0.95%Tensile Stress at Break, ISO 527-1,-2, Injection Molding: 50 to 70 MPaTensile Modulus, ISO 527-1,-2, Injection Molding: 17.5 to 19.5 GPaTensile Strain at Break, ISO 527-1,-2, Injection Molding: 0.4 to 0.5%Charpy Notched Impact Strength, ISO 179, Injection Molding: 2.5 to 4 kJ/m²Charpy Unnotched Impact Strength, ISO 179, Injection Molding: 6 to 8 kJ/m²Compressive Strength, ISO 604: 160 to 190 MPa

Injection instructions

Plastication: 50rpmInjection Time: 2 to 8 secHold Time: 1 to 5 sec/mmCure Time, 0.125 in: 5 to 12 sec/mmAll ISO properties listed were tested in accordance with ISO 3167The value listed as Molding Shrinkage, ISO 294-4, was tested in accordance with ISO 2577.ISO Type: PF 2 C1Powder Density, ISO 60: 0.65 to 0.8 g/cm³Post Shrinkage, ISO 2577: 0.01 to 0.08%HDT A (1.80 MPa) Unannealed, ISO 75A, Injection Molding: 200 to 220°CHDT A (8.0 MPa) Unannealed, ISO 75A, Injection Molding: 175 to 195°CCLTE, Flow (TMA), ASTM E831, Injection Molding: 15 to 25 cm^-6/cm°CCLTE, Transverse (TMA), ASTM E831, Injection Molding: 30 to 40 cm^-6/cm°CFlexural Strength, ISO 178, Injection Molding: 120 to 140 MPaFlexural Modulus, ISO 178, Injection Molding: 13.5 to 15.5 GPaStrain to failure in Flexure, ISO 178, Injection Molding: 0.85 to 0.95%Tensile Stress at Break, ISO 527-1,-2, Injection Molding: 50 to 70 MPaTensile Modulus, ISO 527-1,-2, Injection Molding: 17.5 to 19.5 GPaTensile Strain at Break, ISO 527-1,-2, Injection Molding: 0.4 to 0.5%Charpy Notched Impact Strength, ISO 179, Injection Molding: 2.5 to 4 kJ/m²Charpy Unnotched Impact Strength, ISO 179, Injection Molding: 6 to 8 kJ/m²Compressive Strength, ISO 604: 160 to 190 MPa

Category:	Phenolic , Phenolic
Manufacturer:	Vyncolit N.V.
Trademark:	Vyncolit®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	ab2w3q_Vyncolit-X620-1.pdf
PRICE:	Order Products email sales@su-jiao.com

Resin Grade	Manufacturer	Category	Trademark
Multi-Flex® TPE D3804	Multibase, A Dow Corning Company	TPE	Multi-Flex® TPE
LNP™ THERMOCOMP™ OF008 compound	SABIC Innovative Plastics	PPS, Linear	LNP™ THERMOCOMP™
MAJORIS CG 310 BLACK 8229	AD majoris	PP, Unspecified	MAJORIS
PETILEN G08-21T	PETKIM Petrokimya Holding A.S.	LDPE	PETILEN
Sylvin 9791-75UV Black	Sylvin Technologies Incorporated	PVC, Flexible	Sylvin