OnForce™ LFT NN-40LCF/001 Grey

Category:	Nylon 66 , Polyamide 66
Manufacturer:	PolyOne Corporation
Trademark:	OnForce™ LFT
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	aarndU_OnForce-LFT-NN-40LCF-001-Grey.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

Message
Polyvan's long fiber thermoplastic polymers are used in situations where high hardness and good impact resistance are required, such as metal substitution or other structural applications. These products exhibit enhanced physical and mechanical properties compared to staple fiber products. Its advantages include improved impact strength, elasticity and material strength in different temperature ranges. In addition, compared with traditional high-filled short fiber products, long fiber thermoplastic polymers show improved properties in terms of creep and fatigue resistance, improved dimensional stability and unique surface finish.

General Information
Filler / Reinforcement	Long carbon fiber, 40% filler by weight
Features	Thermal Stability
Forms	Particle

Physical	Nominal Value	Unit	Test Method
Density	1.35	g/cm³	ISO 1183
Molding Shrinkage ¹	0.30	%	ISO 294-4

Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus	29000	MPa	ISO 527-2
Tensile Stress (Break)	305	MPa	ISO 527-2
Tensile Strain (Break)	1.5	%	ISO 527-2
Flexural Modulus	24000	MPa	ISO 178
Flexural Stress	420	MPa	ISO 178

Impact	Nominal Value	Unit	Test Method
Charpy Notched Impact Strength	15	kJ/m²	ISO 179
Charpy Unnotched Impact Strength	55	kJ/m²	ISO 179
Dart Drop Impact	11.8	J	ASTM D5420

Thermal	Nominal Value	Unit	Test Method
Heat Deflection Temperature
1.8 MPa, not annealed	250	°C	ISO 75-2/A
8.0 MPa, not annealed	243	°C	ISO 75-2/C

Injection	Nominal Value	Unit
Drying Temperature	80.0	°C
Drying Time	4.0	hr
Processing (Melt) Temp	290 - 320	°C
Mold Temperature	90.0	°C
Injection Rate	Slow-Moderate
Back Pressure	1.00	MPa

Injection instructions
LFT compounds can be processed using equipment similar to that used for short fiber products. The mechanical properties of finished parts depend greatly on the length of the fibers in the molded part; therefore processing conditions must be set carefully in order to minimize fiber breakage. A "low shear process" is advised, with low back pressure, low screw speed and low-to-medium injection speed.

Injection instructions

LFT compounds can be processed using equipment similar to that used for short fiber products. The mechanical properties of finished parts depend greatly on the length of the fibers in the molded part; therefore processing conditions must be set carefully in order to minimize fiber breakage. A "low shear process" is advised, with low back pressure, low screw speed and low-to-medium injection speed.

Note Message
1 .	Measured on a tensile specimen. Actual mold shrinkage values are highly dependant on part geometry, mold configuration, and processing conditions.

Resin Grade	Manufacturer	Category	Trademark
NuSil GEL1-8155	NuSil Technology	Silicone	NuSil
Devcon Ceramic Repair Putty	Devcon	Epoxy	Devcon
Latiohm 66-08 PD02 G/35	LATI S.p.A.	Nylon 66	Latiohm
LUVOCOM® 50/TF/15/GY04	Lehmann & Voss & Co.	PC	LUVOCOM®
Evoprene™ G 621	Mexichem Specialty Compounds Inc.	TPE	Evoprene™ G